Open Access

In vitro biocompatibility and bioactivity of calcium silicate‑based bioceramics in endodontics (Review)

  • Authors:
    • Wencheng Song
    • Shue Li
    • Qingming Tang
    • Lili Chen
    • Zhenglin Yuan
  • View Affiliations

  • Published online on: May 14, 2021     https://doi.org/10.3892/ijmm.2021.4961
  • Article Number: 128
  • Copyright: © Song et al. This is an open access article distributed under the terms of Creative Commons Attribution License.

Metrics: Total Views: 0 (Spandidos Publications: | PMC Statistics: )
Total PDF Downloads: 0 (Spandidos Publications: | PMC Statistics: )


Abstract

Calcium silicate‑based bioceramics have been applied in endodontics as advantageous materials for years. In addition to excellent physical and chemical properties, the biocompatibility and bioactivity of calcium silicate‑based bioceramics also serve an important role in endodontics according to previous research reports. Firstly, bioceramics affect cellular behavior of cells such as stem cells, osteoblasts, osteoclasts, fibroblasts and immune cells. On the other hand, cell reaction to bioceramics determines the effect of wound healing and tissue repair following bioceramics implantation. The aim of the present review was to provide an overview of calcium silicate‑based bioceramics currently applied in endodontics, including mineral trioxide aggregate, Bioaggregate, Biodentine and iRoot, focusing on their in vitro biocompatibility and bioactivity. Understanding their underlying mechanism may help to ensure these materials are applied appropriately in endodontics.

1. Introduction

The stem cell population in dental pulp possesses multilineage differentiation potential and the pulp vascular system participates in the reaction of dental pulp tissue to external stimulus, the initiation of dental pulp inflammation and pulp tissue repair (1). When sound dentin suffers damage, such as tooth wear, fracture, or caries, bacterial infection and the subsequent inflammatory response lead to damage of pulp tissue and impaired periapical tissue through blood circulation (2). Therefore, endodontic therapy has become a necessary option to preserve teeth by removing microorganisms, their by-products and residual necrotic tissue (3). However, the success rate of traditional endodontic therapy was only 70-80% over the past decade globally (4-6). The apical seal is important to improve the success rate in endodontic therapy; an excellent apical seal by root-end filling prevents the spread of dental pulp inflammation to the periapical tissue (7). In order to achieve a higher success rate in endodontic therapy, an ideal root-end filling material is required that possesses excellent root-end sealing capacity, good biocompatibility with surrounding cells/tissue, superior antibacterial properties and ability to promote tissue regeneration.

Mineral trioxide aggregate (MTA) has been used in root-end filling as calcium silicate-based bioceramic and displays better root apical sealing ability and higher success rates compared with conventional root-end filling materials, such as amalgam and intermediate restorative material (8-10). Furthermore, given its clinical effect in root-end filling in endodontic therapy, MTA has also been used in other endodontic application, such as pulp capping and regeneration and root perforation repair, and is currently considered as the gold standard in endodontics. As ProRoot MTA (Dentsply Sirona) has shown good clinical performance in endodontics, other calcium silicate-based bioceramics have been developed, including Bioaggregate (Innovative Bioceramix, Inc.), Biodentin (Septodont Holding) and iRoot BP/FS/SP (Innovative Bioceramix, Inc.) (11,12).

The chemical constituents of these novel calcium silicate-based bioceramics are similar to that of MTA, but Bioaggregate, Biodentine and iRoot BP/BP Plus display better color stability than MTA because bismuth oxide is replaced by tantalum or zirconium oxide as a radiopacifier. Bioaggregate exhibits superior stable bond strength but inferior mechanical properties and bond strength in comparison with MTA. Biodentine shows increased mechanical strength and longer setting time as it does not contain calcium aluminate and calcium sulfate, which are present in MTA (13). iRoot BP/BP Plus, novel calcium silicate-based bioceramics applied in permanent root canal repair and filling, exhibit easier manipulation and faster setting time compared with MTA (14).

It is essential to clarify the effect and mechanism how these bioceramics influence the surrounding cells/tissue when used in endodontics. Numerous studies have investigated the biocompatibility and bioactivity of bioceramics in endodontics. Materials with good biocompatibility should not induce notable and continuous toxic effects on surrounding cells and tissue (15,16). Biocompatibility can be defined as the interaction between implanted biomaterials and the associated tissue (17). Bioactive materials also induce apatite layer formation and biomineralization (18). Increased deposition of hydroxyapatite over time is observed when calcium silicate-based bioceramics are exposed to PBS, which suggests that these materials are bioactive (19-22). Bioceramics have been demonstrated to have excellent biocompatibility and lasting bioactivity during and after setting by the secretion of molecules. When calcium silicate-based bioceramics are applied in endodontics, the interaction between the materials and cells affect the biological behavior, such as proliferation, differentiation, migration and apoptosis (23,24). Various types of cell are involved in changes of biological behavior when bioceramics are used in endodontics (Fig. 1). For example, calcium silicate-based bioceramics affect the biological behavior of dental pulp stem cells (DPSCs) in dental pulp capping, whereas osteoblasts/osteoclasts are influenced when bioceramics are applied as root-end filling material (25,26). Despite the weakness of in vitro studies in mimicking the human body reaction to environmental stimuli and providing accurate results compared with animal or human studies, it is essential to investigate biocompatibility and bioactivity in vitro to clarify the mechanism underlying how calcium silicate-based bioceramics influence cell behavior. The present review focuses on in vitro biocompatibility and bioactivity when calcium silicate-based bioceramics are applied in endodontics. All information is summarized in Table I.

Table I

In vitro studies of biocompatibility and bioactivity of calcium silicate-based bioceramics in endodontics.

Table I

In vitro studies of biocompatibility and bioactivity of calcium silicate-based bioceramics in endodontics.

BioceramicCell typeSubtypeBiocompatibility and bioactivityReferences
MTAStem cellsDPSCsPromotes proliferation and survival of human DPSCs, BMSCs and PDLSCs via ERK signaling pathway(25)
Concentration- and time-dependent biocompatibility(42-45,48,49,99)
Set MTA shows better biocompatibility than incompletely set MTA(58)
Cells change shape and migrate to form clusters during the first week, and apparent mineralization at day 21 following induction with MTA(62)
Begin to differentiate at day 7 following induction with MTA(63)
Affect more genes in uninduced DPSCs than in DPSCs induced by odontogenic differentiation medium(64)
Promotes odonto/osteogenic differentiation via p42/44 ERK and NF-κB pathways(42,44)
Enhances formation of collagen fibers and mineralized nodules(65,66,70)
Increases secretion of angiogenic factors, such as VEGF(63)
PDLSCsBioroot BC Sealer is more biocompatible than Endoseal MTA and MTA Fillapex(100-102)
Induces odonto/osteogenic differentiation by activating NF-κB and MAPK pathways(103)
BMSCsRespond more rapidly to MTA than human PDLSCs and PSCs(25)
Rat BMSCs respond more rapidly to MTA than human BMSCs(107-109)
Induces proliferation and odonto/osteoblastic differentiation in a dose-dependent manner via ERK and JNK signalling pathways(25,110,111)
SHEDEnhances attachment, proliferation, migration and odontogenic differentiation(125,126)
Fresh mixed MTA and direct incubation with MTA induce cytotoxicity(130)
SCAPs Concentration-/time-dependent biocompatibility(25,133-135,138)
Induces odonto/osteogenic differentiation via NF-κB, p38 and ERK signaling(138-140,142)
Increases expression of pro-inflammatory cytokines IL-1α, IL-1β and IL-6(139)
Increases expression of angiogenic genes VEGFA and FIGF/VEGFD(134)
TGSCsBiocompatible and increases release of PDGF, FGF-2 and VEGF(73)
Direct incubation with MTA inhibits viability and odontogenic differentiation(151)
OsteoblastsPrimary osteoblastsInhibit cell proliferation and differentiation(156-158)
Biocompatible with primary osteoblasts cultured in 3D culture system and promotes differentiation(166)
MC3T3-E1Promotes viability, osteoblastic differentiation and by activating transcription factor 6 and endoplasmic reticulum stress response(168-171)
MG-63Cytotoxicity and inflammation decrease as material sets(167,174)
Saos-2Promote the adhesion, spreading, proliferation and secretion of collagen(176,177)
Enhances osteogenic differentiation(178)
OsteoclastsOsteoclastsInhibits bone resorption and osteoclast differentiation by preventing migration and fusion of osteoclast precursors via attenuation of the autophagic pathway(191,193,194)
Inhibit osteoclastogenesis dose-dependently(195,196)
FibroblastsDPCsMore biocompatible with rat pulp cells (RPC-C2A) than SuperEBA and Vitrebond(218)
Promotes proliferation and odontogenic differentiation, and decreases secretion of IL-1β and IL-6(219,220)
Enhances expression of VEGF and angiogenin(222)
DPFsLess cytotoxic than Ca(OH)2(232)
No cytotoxicity or genotoxicity(233)
PDLCsInhibits proliferation, viability and differentiation(111,244)
Enhances calcification and BMP-2 expression(245)
PDLFsFresh MTA inhibits proliferation, attachment and differentiation of PDLFs(250-253)
More biocompatible than commonly used endodontic materials(105,254-257)
Induces differentiation(105)
Concentration-/time-dependent biocompatibility(251,258-261)
Immune cellsMonocytic cellsBiocompatible with THP1 cells and increases secretion of cytokines by THP1 cells(272)
Induces THP-1 polarization toward M2 phenotype by activating Axl/Akt/NF-κB signaling pathway(286)
NeutrophilsIncreases expression of IL-1β and IL-8(278)
Enhances chemotaxis and chemokinesis by activation of calcium-sensing receptors and downstream pathways(279)
MacrophagesInduces release and upregulates expression of neutrophil chemotactic factor substances from macrophages and mast cells(275-277)
Biocompatible(282-284)
Increases expression of inflammatory cytokines and induces M2 polarization in RAW 264.7 macrophages(282,285)
LymphocytesNo DNA breakage to human peripheral lymphocytes(287)
BioaggregateStem cellsBMSCsBiocompatible(115)
OsteoblastsMC3T3-E1Shows no cytotoxicity and increases expression of COL1, OCN and OPN(180)
OsteoclastsOsteoclastsSimilar ability to MTA to prevent migration and fusion to inhibit bone resorption and differentiation via NF-κB signaling pathway(191-193)
FibroblastsDPCsSimilar compatibility and ability to enhance odontogenic differentiation by activation of MAPK signaling pathway to MTA(223,224,226)
Superior to MTA in promoting cell adhesion and migration(225)
Stronger potential to induce osteogenic differentiation than MTA(223)
PDLCsBetter biocompatibility than MTA(246)
Promotes mineralization and osteogenic differentiation in a concentration-/time-dependent manner via miR-146a(247)
PDLFsComparable biocompatibility with MTA(262)
BiodentineStem cellsDPSCsSuperior to MTA in biocompatibility and mineralized nodule formation(74,82,86)
Promotes osteo/odontogenic differentiation and mineralization by activating ERK1/2 and JNK, and attenuating NF-κB pathways(53,75-78)
No effect on expression of IL-6 and IL-8 but decreases expression of TGF-β(53)
More compatibility when stored in acid rather than saline(58)
Slight toxicity and more odontogenic differentiation when directly contacting DPSCs(49,77,80)
Similar ability to improve expression of VEGF compared with MTA(49)
PDLSCsSimilar dose-dependent biocompatibility to MTA(104)
BMSCsPromotes proliferation(116-118)
Inferior to MTA in promoting proliferation and osteoblastic differentiation(119)
SHEDSimilar dose-dependent biocompatibility to MTA(126,126,128,129)
Superior to MTA in promoting proliferation and calcified matrix deposition(125,127)
SCAPsSimilar biocompatibility to MTA(133,134,136)
Induce odonto/osteogenic differentiation in dose-dependent manner(138,139)
Superior to MTA in inducing odontoblastic differentiation(133,134,137)
Similar capacity to enhance expression of pro-inflammatory cytokines, such as IL-1α, IL-1β, IL-6 and TNF-α, compared with MTA(139)
Similar ability to promote expression of VEGFA and FGIF(134)
TGSCsSimilar to MTA in biocompatibility and release of angiogenic(73)
OsteoblastsPrimary osteoblastsSimilar cytocompatibility to MTA(164,181)
MG-63Similar cytocompatibility to MTA(182)
MC3T3-E1Similar ability to promote calcification compared with MTA(183)
Saos-2Similar dose-dependent biocompatibility to MTA and induces expression of ALP and mineralization(184)
OsteoclastsOsteoclastsLower inhibitory effect on differentiation and activity via ERK1/2 and NF-κB signaling pathways(197)
FibroblastsDPCsBiocompatible and promotes odontoblastic differentiation and biomineralization(224,229)
Similar ability to MTA in increasing TGF-β1 secretion(228)
DPFsSimilar biocompatibility to MTA in concentration-/time-dependent manner(233,234)
Affects differentiation in a concentration-dependent manner by modulating TGF-β1 secretion(228,234)
More biocompatibility and less inflammation compared with TheraCal(78,240,243)
PDLCsSimilar biocompatibility to MTA(55,181)
Superior to MTA in terms of attachment and proliferation(181)
PDLFsViability increases with time(261)
More cell aggregates on surface compared with MTA(267)
Higher expression of Integrin β1 and Vinculin compared with MTA(268)
Immune cellsMonocytesDecreases adhesion of THP-1 cells to endothelial cells, migration and activation to macrophages(240)
Similar biocompatibility compared with MTA(289)
MacrophagesNo effect on activation and inflammatory response of THP-1 macrophages(288)
Greater inhibitory effect on expression of inflammatory cytokines compared with MTA(183)
iRoot BP PlusStem cellsDPSCsGreater ability to promote adhesion, migration and mineralization than MTA(93)
Similar ability to enhance formation of focal adhesions and reorganization of the actin cytoskeleton compared with MTA(94)
BMSCsEnhances osteo/odontogenic differentiation via MAPK pathway and autophagy(114)
SHEDSimilar in promoting proliferation but superior in enhancing migration, adhesion and osteogenetic differentiation(93)
OsteoblastsPrimary osteoblastsMore cytotoxic than MTA(185)
MC3T3-E1Improved viability under inflammatory acidic environment compared with MTA(186)
FibroblastsDPCsSuperior to MTA in proliferation, mineralization and odontoblastic differentiation(226,230)
Promotes migration and upregulates expression of focal adhesion molecules via FGFR-mediated ERK 1/2, JNK and Akt pathways(231)
iRoot FSStem cellsDPSCsPromotes proliferation, migration and osteogenic differentiation(97)
Superior to Biodentine in terms of proliferation and migration(98)
SCAPsSimilar biocompatibility but stronger capacity to enhance migration and osteo/odontogenesis via the Wnt/β-catenin pathway in comparison with MTA(147)
OsteoblastsMC3T3-E1More biocompatible than iRoot BP Plus or MTA(187)
MG63More biocompatible than iRoot BP Plus or MTA(188)
FibroblastsPDLCsSuperior to Biodentine in cell viability, proliferation and osteogenic differentiation(248)
iRoot FMStem cellsSCAPsInduces proliferation and osteo/odontogenic differentiation dose-dependently without affecting cell morphology(148)
iRoot SPStem cellsTGSCsBiocompatible(152)
Inferior to MTA in inducing odontogenic differentiation and hard tissue deposition(153)
OsteoblastsMG63Biocompatible and enhances expression of COL1, OCN and BSP(190)
OsteoclastsOsteoclastsMore cytotoxicity than MTA, but similar potential to inhibit osteoclastogenesis(200)
FibroblastsPDLCsDisplays biocompatibility and enhances osteoblastic differentiation via the integrin-mediated signaling pathway(249)
Immune cellsMacrophagesMore cytotoxic and primarily induces M1 macrophage polarization compared with MTA(200)
Similar ability to MTA in enhancing expression of inflammatory cytokines in RAW 264.7 macrophages(200,282,285)
Similar ability to shift balance of M1/M2 polarization to M2 polarization compared with MTA(282,285)

[i] MTA, mineral trioxide aggregate; DPSCs, dental pulp stem cells; DPCs, dental pulp cells; DPFs, dental pulp fibroblasts; PDLSCs, periodontal ligament stem cells; PDLCs, periodontal ligament cells; PDLFs, periodontal ligament fibroblasts; BMSCs, bone marrow stromal/stem cells.

2. Stem cells

Mesenchymal stem cells (MSCs) derived from dental tissue originate from teeth and surrounding support tissue, possess similar biological characteristics to bone marrow-derived MSCs and differentiate into osteoblasts, adipocytes, chondrocytes and neural cells (27,28). MSCs derived from dental tissue are capable of dentinogenesis or angiogenesis and secretion of growth factors, which influence behavior, such as proliferation, differentiation and mineralization (29). MSCs derived from dental tissue include DPSCs, periodontal ligament stem cells (PDLSCs), stem cells from human exfoliated deciduous teeth (SHED) and stem cells from apical papilla (SCAPs) that are involved in renewal and regeneration of dental tissue via the repair of injured dentin, root structure and the pulp-dentin complex (26,30,31) (Fig. 2). Calcium silicate-based bioceramics significantly promote attachment and survival of stem cells derived from dental tissue but their effects on biological behavior appear to be cell type-dependent (25). Several common markers are used to test the osteo/odontogenic and angiogenic potential of stem cells in the presence of calcium silicate-based bioceramics. For example, alkaline phosphatase (Alp) is a marker protein of mineralization and is associated with early osteo/odontogenic differentiation (32,33). Collagen type I (COL1), osteocalcin (Ocn) and osteopontin (OPN) are expressed in the extracellular matrix and serve an important role in osteoblastic mineralization (34). Runt-related transcription factor 2 (Runx2) acts as a marker of osteogenesis in the early stage (35,36), while Ocn functions in the late stage of osteogenic differentiation (37,38). Regarding dentinogenesis, Runx2 and its downstream molecule osterix (Osx), dentin sialoprotein and dentin sialophosphoprotein (DSPP) and its downstream molecule dentin matrix protein 1 (DMP1) (39,40) are considered as protein markers closely associated with the formation and mineralization of odontoblasts.

DPSCs

MTA promotes the proliferation and survival of human DPSCs, bone marrow stromal/stem cells (BMSCs) and PDLSCs via the ERK signaling pathway (25), and also exhibit a positive effect on viability of human DPSCs (41). MTA at high concentrations (20 and 10 mg/ml) is toxic to human DPSCs but MTA at low concentrations (2.0, 1.0, 0.2 and 0.1 mg/ml) enhances viability of human DPSCs but has no effect lower concentrations (0.020 and 0.002 mg/ml) (42). Similarly, undiluted MTA extract slightly increase survival of human DPSCs, while 1/2 and 1/4 dilutions of MTA extract have no effect on cell viability (43). In addition, MTA at high concentrations (20 mg/ml) decreases proliferation of DPSCs under inflammatory conditions but has no effect at low concentrations (0.020 and 0.002 mg/ml) (44). Moreover, various commercial MTA extracts, such as Angelus MTA (Angelus Dental Products Industry) and Root MTA (University of Tabriz, Iran), show similar effects on human DPSCs but were more biocompatible when applied at lower concentration (1:2) and longer exposure times compared with MTA. These results suggested that the biocompatibility of MTA is dependent on not only dosage but also exposure time (45). In terms of time-dependent biocompatibility of MTA, the cytotoxicity of MTA decreased over time and the viability and proliferation of human DPSCs increased following two aging cycles, which further supported the aforementioned time- and concentration-dependent effects of MTA (46). Moreover, the proliferation and viability of DPSCs decreased significantly when in direct contact with MTA for the first day but subsequently raised after three days (47). The initial cytotoxicity of MTA to growth and viability of DPSCs (47-49) may be partly ascribed to the relatively rough surface of biomaterials (50) or leakage of components such as bismuth oxide (51) and Al (52) and Si ions (53). Higher levels of Si ion concentrations from the SiO2 phase of materials may lead to hyperosmoticity and subsequently stimulates production of inflammatory cytokines (54). Furthermore, production of MTA during the hydration reaction and its exposure concentration may result in early slight cytotoxicity of MTA. Calcium hydroxide is produced when calcium silicate contained in MTA reacts with water and increases pH of the culture media (55,56). Basic pH environment and release of inorganic salts induced by high concentrations of MTA significantly decreases cell proliferation (57). Furthermore, 24-h set MTA promotes viability of human DPSCs, whereas 1-h set MTA exhibits an inhibitory effect after 7 days, which suggests that incompletely solidified MTA is cytotoxic (58). The subsequent rise in cell viability may be caused by hydroxyapatite layer formation on the hydrated bioceramic surface (59) controlled continuous production of calcium, silica and phosphate ions from bioceramics along with alkaline pH in the later stage (60,61). Regarding differentiation of human DPSCs, in the first week following induction with MTA in odontogenic differentiation medium, DPSCs began to change from spindle to rounded shape upon reaching confluency and then migrated to form clusters (62). DPSCs began to differentiate at day 7 (63) and mineralization was observed by Alizarin Red staining until day 21. Combination of MTA and odontogenic differentiation medium enhanced odontogenic differentiation of DPSCs but MTA extract-alone did not induce this (62). Treatment with MTA for 1 day affected more genes in uninduced DPSCs than in DPSCs induced by odontogenic differentiation medium, which suggested that MTA exhibits a greater stimulative effect on odontogenic differentiation of uninduced DPSCs compared with induced DPSCs (64). In addition, MTA at a concentration of 0.2 mg/ml displayed the strongest capacity to induce odontoblastic differentiation of human DPSCs via the p42/44 ERK signaling pathway (42). MTA-conditioned medium at the same concentration enhances the odonto/osteogenic capacity of DSPCs from inflammatory sites by activating the NF-κB pathway, as shown by significantly upregulated odonto/osteoblastic gene expression levels, such as ALP, RUNX2, OSX, OCN and DSPP (44). Consistent with the changes in genes associated with osteo/dentinogenic differentiation, MTA promotes mineralized nodule formation of human DPSCs (65,66). Increased secretion of angiogenic factor VEGF has been detected in human DPSCs induced by MTA (63), which in turn affects viability and function of DPSCs (67). MTA contributes to dentin bridge formation in endodontics (68,69). In addition, MTA is applied in pulp capping because of its excellent bioactivity, which has been confirmed by the elongated shape of DPSCs, formation of collagen fibers and calcified deposition in the presence of MTA in a model simulating indirect pulp capping (70). In previous studies, accelerants, including 5% CaCl2 and 2.5% Na2HPO4, have been mixed with MTA to shorten setting time. Compared with MTA in the presence of distilled water, MTA in the presence of 5% CaCl2 and 2.5% Na2HPO4 is more biocompatible and exhibits greater ability to promote odontoblastic differentiation of DPSC niches (48,71). Propolis, a natural alternative endodontic material produced by honeybees from tree resin, also enhances the ability of MTA to promote odontogenic differentiation and mineralization of DPSCs via the ERK pathway (72).

Compared with human PDLSCs and tooth germ stem cells (TGSCs), human DPSCs exhibit better viability in the presence of both Biodentine and MTA (73). Moreover, Biodentine displays a superior ability to promote viability, adhesion and migration of human DPSCs compared with MTA. Human DPSCs spread on the surface of Biodentine show a spindle, polygonal and flattened morphology (74). Similar to MTA, high concentrations of Biodentine extract (20 mg/ml) exhibit slight cytotoxicity, whereas 0.2 mg/ml Biodentine enhances biological behaviors of human DPSCs, including cell proliferation, viability, migration, adhesion and mineralization formation. In addition, low concentrations of Biodentine (0.2 mg/ml) promote odontoblast differentiation and biomineralization of human DPSCs by activating ERK1/2 and JNK and attenuating the NF-κB pathway (75,76). Increased Alp activity and dentin matrix protein expression levels have been observed in human DPSCs stimulated with Biodentine (75-78). Furthermore, Biodentine significantly increases calcium deposition (79) and enhances the production of Ocn and Runx2 in human DPSCs stimulated with lipopolysaccharide (LPS) although there is no change in ALP expression levels (53). In terms of the inflammatory response, Biodentine does not affect high expression of IL-6 and IL-8 in DPSCs induced by LPS stimulation but decreases levels of the anti-inflammatory cytokine TGF-β1 (53). Although Biodentine medium is biocompatible with DPSCs, when in direct contact with DPSCs, Biodentine exhibits a slight toxic effect and delays closure of wound edges, which implies that direct contact between Biodentine and DPSCs leads to cell death or decreased proliferation (80,81). However, unaltered expression levels of actin, tubulin and vimentin indicate that Biodentine neither induces apoptosis, inflammation and genotoxicity nor impairs cellular architecture. The inhibitory effect of Biodentine on cell proliferation and migration may result from the decreased space for cell growth in a direct culture model and prolonged cell doubling time (80). Similarly, other studies have observed that the viability of human DPSCs in direct contact with Biodentine is initially decreased (49,77), which may be due to substantial calcium ion released from Biodentine in the first 3 h (82). Relatively large amounts of Ca and Si ions and the absence of Sr, Al and S in Biodentine extract contribute to the biocompatibility of Biodentine (74). Considering the increased release of Ca and Si ions (83) and microstructural (84,85) changes induced by acidic conditions, human DPSCs cultured in Biodentine stored in acidic environment display more spindle-shaped formation and higher adherent cell density compared with that in Biodentine stored in saline (58) Similar to MTA, Biodentine also increases gene expression levels of osteogenic and odontogenic markers, such as OPN and DSPP in human DPSCs when in direct contact with DPSCs (49,77). However, Biodentine promotes odontogenic differentiation of DPSCs more significantly than osteogenic differentiation, as indicated by detection of expression levels of odontoblastic marker DSPP and osteogenic gene markers ALP, COL1A1 and OPN (80). Moreover, Biodentine promotes biomineralization and secretion of extracellular mineral matrix in human DPSCs cultured with osteogenic medium for 21 days (77) and induces more mineralized nodules in the osteogenic medium compared with MTA, suggesting that increased calcium ion release, along with a neutral pH, promotes differentiation and mineralization of DPSCs and subsequently generates a greater number of structured dentin bridges (82). Similarly, when DPSCs are cultured with three-dimensional models, Biodentine induces higher viability compared with MTA. Furthermore, expression levels of COL1A1, ALP and DSPP in DPSCs on MTA and Biodentine are initially upregulated significantly and then decrease gradually until day 21; however, expression of RUNX2 in three-dimensional cultures remains lower than that in control group (86). The reason for this may be that COL1A1, ALP and DSPP are associated with initiation of dentinogenesis and mineralization. Low expression levels of RUNX2 contribute to odontoblast differentiation and cell maturation, whereas increased expression is observed during terminal odontoblast differentiation (87,88). MTA and Biodentine stimulated angiogenesis by improving the expression levels of VEGF in human DPSCs on day 14 (49). VEGF enhances the proliferation, migration, and tubulogenesis of endothelial cells close to microvessels, which regulates both vascularization and angiogenesis. Angiogenesis is a key factor for wound healing and tissue regeneration of damaged dental pulp (89-91). The pro-angiogenic capacity of bioceramics depends on dissolution products, such as Si, Mg and Ca ions, which induce secretion of angiogenic factors from cells. Dissolution of calcium ions and subsequent precipitation reactions on the surface of bioceramics leads to vascular penetration and osteoblastic differentiation. Interconnections and pore size of the scaffold also influence the size and amount of the blood vessels, which are necessary for the vascularization of bioceramic material (92).

iRoot BP Plus promotes proliferation, attachment, migration and mineralization of DPSCs compared with MTA (93). Furthermore, iRoot BP Plus releases more Si ions than MTA, which may explain why iRoot BP Plus induces greater apatite formation. iRoot BP Plus and MTA promote stretched and highly organized stress fibre assembly of DPSCs, which is indicative of reorganization of the actin cytoskeleton. Moreover, iRoot BP Plus and MTA enhance phosphorylation of both Paxillin and focal adhesion kinase (FAK) and increase protein expression levels of Vinculin, FAK and Paxillin in human DPSCs (94); this is associated with the formation of focal adhesions (95). Cytoskeleton reorganization and focal adhesion formation is essential for cell adhesion and migration (96). These results confirmed that both iRoot BP Plus and MTA promote attachment and migration of human DPSCs. Likewise, iRoot FS enhances proliferation, migration, and osteoblastic differentiation of human DPSCs (97). Additionally, iRoot FS displays superior ability than Biodentine to promote proliferation and migration of human DPSCs on day 7. However, iRoot FS showed no significant effect on osteogenic differentiation on day 7 (98), which implied that iRoot FS affects proliferation and migration of human DPSCs and later influenced osteoblastic differentiation. A longer experimental observation period should be used to investigate the bioactivity of calcium silicate-based bioceramics on human DPSCs.

PDLSCs

MTA exhibits concentration-dependent cellular compatibility with human PDLSCs; MTA at higher dilution exhibits better biocompatibility with human PDLSCs (99). Due to the biological characteristics of MTA, other MTA-based endodontic materials have been developed, including Endoseal MTA (ES; Maruchi Co., Ltd.), Nanoceramic Sealer (NCS; B&L Biotech USA, Inc.), Bioroot BC Sealer (BR; Septodont Holding) and MTA Fillapex (Angelus Dental Products Industry). Although human PDLSCs in the presence of these MTA-based bioceramics maintain high expression levels of MSC markers, including CD105, CD73 and CD90, the capacity of human PDLSCs to migrate, adhere and grow is higher when treated with BR at different concentrations compared with ES and NCS. ES and MTA Fillapex show cytotoxicity to human PDLSCs at 24, 48 and 72 h and give rise to worse cell attachment and spread, which may be caused by tungsten contained in MTA Fillapex (100-102). By contrast, 2 mg/ml MTA extract is the optimal concentration to markedly increase calcified nodule formation, Alp activity and odonto/osteogenic differentiation in human PDLSCs; these effects are mediated by activating NF-κB and MAPK signaling pathways (103). Likewise, 2 mg/ml Biodentine is the most biocompatible concentration to promote migration, attachment, and mineralization of human PDLSCs. Biodentine at low concentrations (2.00, 0.20 and 0.02 mg/ml) significantly enhances viability of human PDLSCs, while Biodentine at higher concentrations (20 mg/ml) exhibits cytotoxicity, which may be associated with high pH (104). High pH of Biodentine results in an increased concentration of iron and calcium ions in the extracellular environment (105). The inhibitory effect of Biodentine at high concentration (20 mg/ml) on the viability of human PDLSCs may be explained by increased or unbalanced ions levels, which generate a toxic effect on cells (106).

BMSCs

BMSCs are used as an in vitro model of MSCs associated with wound healing and tissue regeneration of alveolar bone. MTA promotes the adhesion and proliferation of human DPSCs, PDLSCs and BMSCs, which display an elongated morphology and are well-spread. Moreover, positive effects of MTA on proliferation are cell type-dependent (25). Human PDLSCs and DPSCs rapidly respond to MTA with significantly increased cell number by day 3, whereas human BMSCs stimulated with MTA show slow increase by day 5 (25). Furthermore, MTA promotes migration of human BMSCs significantly after 18 h and cells spread well on the surface of MTA after 24 h. MTA increases proliferation of human BMSCs when incubated in normal medium, whilst the same phenomenon was delayed by 7 days when cultured in differentiation medium (107). When human BMSCs are cultured in osteogenic differentiation medium, MTA does not stimulate osteogenic differentiation by day 10, as indicated by decreased mRNA and protein expression levels of osteogenic markers, such as RUNX2, OSX, MSX2 and OCN (108). A positive effect of MTA on viability of rat BMSCs is observed up to day 7, which is sooner than in human BMSCs. Simultaneously, MTA stimulates rat BMSC differentiation into osteoblast-like cells over 7 days, which is confirmed by enhanced ALP staining and upregulation of gene expression levels of bone morphogenetic protein 2 (BMP-2), ALP, bone sialoprotein (BSP) and osteocalcin (OC) (109). Low concentrations of MTA-conditioned media (2.000, 0.200, 0.020 and 0.002 mg/ml) are not toxic to BMSCs and 0.02 mg/ml MTA is the optimal concentration to upregulate odonto/osteogenic capacity of BMSCs originating from rat mandible; this finding was supported by enhanced Alp activity, calcified nodule formation and expression levels of odonto/osteoblastic genes in BMSCs, such as ALP, RUNX2, OSX, OCN and DSPP. However, MTA at lower dilution inhibits the proliferation of BMSCs (110). Likewise, 1:5 MTA medium decreases viability and osteogenic differentiation of primary BMSCs from the hind limb of mice, as indicated by decreased von Kossa staining and low expression levels of OCN and BSP (111). Furthermore, tricalcium aluminate, a primary composite of MTA, contains aluminum and exhibits significant toxicity to rat BMSCs from femur and tibia bone marrow in vitro, whereas good tissue compatibility has been observed with tricalcium or dicalcium silicate (112). In addition, bismuth oxide in MTA is cytotoxic to human BMSCs (113). Therefore, the negative effect of MTA on the viability of BMSCs at high concentrations may partly be caused by tricalcium aluminate and bismuth oxide. Investigation of the mechanism underlying how MTA affects behavior of BMSCs has demonstrated that the ERK signaling pathway is associated with the positive effect of MTA on proliferation (25) and odonto/osteogenic differentiation of BMSCs. JNK signaling pathway is also involved in the odonto/osteogenic capacity of BMSCs induced by MTA (110). In addition, iRoot BP Plus promotes osteogenic/odontogenic differentiation of BMSCs via the MAPK signaling pathway and autophagy (114).

Bioaggregate is non-toxic to human BMSCs throughout a culture period of 24 h (115). Similarly, Biodentine promotes proliferation of rat (116) and human BMSCs (117,118). Both Biodentine and MTA at high concentrations (1:2) show cytotoxicity to human BMSCs, while Biodentine at low concentrations (1:10 and 1:20) and long incubation periods exhibits an inferior ability to enhance proliferation and osteoblastic differentiation of human BMSCs compared with MTA (119). Moreover, Biodentine and MTA display an inhibitory effect on survival of human BMSCs in a concentration-dependent manner over 7 days but do not affect cell morphology (120). The cytotoxicity of Biodentine to human BMSCs may be ascribed to the calcium chloride contained in its liquid (121), which has been reported to exhibit less biocompatibility when added to MTA compared with MTA mixed with water (122). Therefore, Biodentine prepared following complete setting is more compatible with human BMSCs than MTA (120). High Alp activity with mineral deposits in rat BMSCs have been found in the presence of Biodentine after 12 days (116) but the capacity of Biodentine to induce osteogenic differentiation in human BMSCs is inferior to that of MTA (117,118). MTA exhibits earlier and more pronounced calcium deposits than Biodentine (120), which may be explained by the fact that MTA produces high pH and Alp activity and promotes production of high concentration of Ca ions (123).

SHEDs

SHEDs originate from deciduous teeth and regenerate bone and dentin, but not dentin/pulp-like complexes as human DPSCs do (124). Due to the good porous microstructures in MTA or Biodentine, SHEDs attach and spread well on the surface of MTA and Biodentine, which helps SHEDs maintain mesenchymal properties in the presence of MTA or Biodentine with positive expression of CD105, CD90 and CD73 (125). Moreover, the capacity of SHEDs to adhere and proliferate is enhanced by MTA or Biodentine after 48 h (125). MTA and Biodentine exhibit a comparable ability to promote migration of SHEDs. In addition, the viability and proliferation of SHEDs cultured with 1 mg/ml MTA- or Biodentine-conditioned medium is similar to that of negative control during the whole incubation period, which implies that both MTA and Biodentine at 1 mg/ml are non-toxic to SHEDs (126). However, MTA shows greater potential to promote odontogenic differentiation compared with Biodentine (126), whereas Biodentine has better capability to promote proliferation and calcified matrix deposition in SHEDs than MTA (125,127). Furthermore, Biodentine affects behavior of SHEDs in a concentration-dependent manner. Biodentine at low concentrations (2.00, 0.20 and 0.02 mg/ml) stimulates proliferation, viability and migration of SHEDs, whereas high concentrations of Biodentine (20 mg/ml) exhibit slight cytotoxicity to SHEDs. Changes in the concentration of Biodentine have no impact on the adhesion ability of SHEDs (128). Similarly, Biodentine at higher dilutions (1:16 and 1:32) is more effective in promoting proliferation, odontogenic differentiation and biomineralization of SHEDs, which may be because Sr and Si are gradually released from Biodentine as the concentration of Biodentine decreases over time (129). By contrast, fresh mixed MTA impairs the viability and migration of SHEDs and enhance apoptosis over 7 days. Furthermore, the cytotoxicity of MTA to SHEDs is more apparent when SHEDs directly contact MTA (130). The different results may be associated with the preparation of MTA. For example, freshly mixed MTA is frequently used in endodontics whereas bioceramic eluate or aged bioceramics were used in the aforementioned in vitro studies (86). However, the cytotoxicity of these bioceramics generally decreased as the bioceramic set and pH changed of medium over time. Freshly mixed MTA caused severe damage to cells due to the initially high concentration of calcium hydroxide and subsequent raise in pH to 12.5 after mixing for 3 h (131,132). Although iRoot BP Plus possesses a similar capacity to MTA in terms of SHEDs proliferation, it displays more prominent capacity to enhance adhesion, migration and osteogenesis of SHEDs compared with MTA (93).

SCAPs

Both MTA and Biodentine have been shown to promote the proliferation, odontoblastic differentiation and biomineralization of SCAPs over 14 days (133,134). However, Schneider et al (135) found MTA induces early short-term proliferation of SCAPs over 5 days and promotes the migration of SCAPs after 6 h. Saberi et al (136) discovered that the cytotoxicity of both complete set MTA and Biodentine to SCAPs decreased over time. By contrast, Miller et al (137) revealed that incompletely set MTA inhibits proliferation of SCAPs, whereas Biodentine promotes proliferation of SCAPs. The difference in results may be due to the method of cytotoxicity assessment, contact between cells and material, concentration of material and assessment time points. MTA affects survival of SCAPs in concentration-dependent manner. MTA at lower concentrations (0.02, 0.20 and 2.00 mg/ml) exhibits excellent biocompatibility with SCAPs; however, proliferation of SCAPs is inhibited and normal morphological cells disappeared when treated with MTA at higher concentrations (10 and 20 mg/ml) (138). Low concentrations of MTA or Biodentine (2.00, 0.20 and 0.02 mg/ml) enhance Alp activity and osteoblastic/odontoblastic differentiation in SCAPs, while high concentrations of MTA or Biodentine (20 mg/ml) exhibit a negative effect (138,139). MTA extract enhances the ability of osteogenic medium to induce mineralization and increase expression of mineralization-associated genes, such as Ocn (140). In comparison with MTA, SCAPs treated with Biodentine display greater odontoblastic differentiation, as demonstrated by positive alizarin red staining and expression of genes encoding DMP-1, DSPP, OCN and matrix extracellular phosphoglycoprotein (133,134). Biodentine enhances expression of odontoblast specific marker DSPP, while MTA promotes osteoblastic differentiation of SCAPs by increasing expression of the osteoblastic marker integrin-binding sialoprotein (137). Both MTA and Biodentine enhance the secretion of pro-inflammatory cytokines, such as IL-1α, IL-1β and IL-6 (139), and MTA activates NF-κB signaling pathway, which affects the odonto/osteogenic differentiation of SCAPs (141,142). In addition, p38 and ERK signaling pathways serve an essential role in odontoblastic/osteoblastic differentiation of SCAPs stimulated by MTA (138). MTA and Biodentine enhance the angiogenic potential of SCAPs; these bioceramics promote the expression of angiogenic genes in human SCAPs, such as VEGFA and c-fos induced growth factor (FIGF) (134), which induce endothelial cell proliferation, migration and differentiation, and promote formation of endothelial tubules (143-146).

Compared with MTA, iRoot FS exhibits similar biocompatibility with human SCAPs but possesses markedly stronger capacity to enhance migration and osteo/odontogenesis differentiation of human SCAPs, and mineralized nodule formation via the Wnt/β-catenin signaling pathway (147). iRoot FM at low concentrations (0.5 mg/ml) increases proliferation and osteo/odontoblastic differentiation of SCAPs, whereas there is no marked effect on SCAPs stimulated with iRoot FM at high concentrations (1.0 and 2.5 mg/ml). Moreover, mineralized nodule formation and expression of DMP-1 and ALP are enhanced by iRoot FM compared with Ca(OH)2. However, iRoot FM at different concentrations has no impact on morphology of SCAPs (148).

Human TGSCs

TGSCs, a popularized stem cell source derived from wisdom teeth, display MSC properties and can differentiate into endothelial or epithelial cells in dental tissue regeneration (149,150). Consistent with human DPSCs and PLSCs, MTA and Biodentine exhibit no cytotoxicity to TGSCs (73). Nonetheless, viability and odontogenic differentiation of TGSCs are inhibited slightly when in direct contact with MTA, which has been confirmed by decreased numbers of attached cells and Alp activity (151). MTA and Biodentine induce angiogenesis of TGSCs by promoting the release of angiogenic growth factors (platelet-derived growth factor, fibroblast growth factor-2 and VEGF) and enhancing tube formation of human umbilical vein endothelial cells (73). Furthermore, iRoot SP exhibits good biocompatibility with human TGSCs and promote their attachment (152). iRoot SP possesses an inferior capacity to MTA in terms of inducing odontogenic differentiation of human TGSCs and hard tissue deposition; human TGSCs in the presence of MTA exhibit higher Alp activity and enhanced odontoblastic differentiation compared with those in the presence of iRoot SP (153).

3. Osteoblasts/osteoclasts

Restoration of bone tissue around teeth with lesions relies on the amount of, and balance between, osteoblasts and osteoclasts (154). When calcium silicate-based bioceramics are used in perforation repair, apical plugs in necrotic teeth or root-end filling in endodontics, the interaction between the bioceramics and osteoblasts in periapical tissue is key to inflammation control and wound repair of (155). The biological influence of calcium silicate-based bioceramics on osteoblasts/osteoclasts must be characterized.

Osteoblasts

Proksch et al (156) found that MTA impairs proliferation, osteogenic differentiation and extracellular matrix mineralization of primary human osteoblasts derived from the alveolar bone; this could be restored by addition of fluoride to MTA. Similarly, MTA inhibits proliferation and COL1 gene expression in bone marrow osteoblasts from rat femur (157). MTA inhibits proliferation and differentiation of rat primary calvarial osteoblasts, as demonstrated by decreased calcified nodule formation and osteoblastic differentiation (158). When primary osteoblasts are cultured with MTA, the highest ionic concentration in areas around MTA results in an inhibitory effect on primary osteoblasts in the central area (158). High dissolution rate of MTA and large release of calcium hydroxide from MTA contribute to highest ionic concentration in areas around MTA (159). Excess calcium concentration induces cell death by apoptosis or necrosis (160), whereas slight increases in extracellular Ca2+ concentration (161) and continuous low levels of calcium ion release, along with slower change in pH, promote proliferation and differentiation of osteoblasts (162,163). The decreased viability of primary human osteoblasts induced by MTA may be due to the cumulative effect of the release of toxic components, such as Bi and Al ions, following contact with bioceramic extract (164). These different results may be due to different methods and concentrations of bioceramics used in the experiments. MTA exhibit higher biocompatibility with osteoblasts cultured in three-dimensional culture systems and are attracted toward the material compared with cells cultured directly on materials or in extract. Increased percentage of mature osteoblasts or osteocytes with high expression levels of green fluorescent protein and osteogenic genes, including ALP, BSP and OSX, in primary mouse mandibular osteoblasts demonstrates that MTA promotes differentiation of primary mouse osteoblasts in a three-dimensional cell culture model without differentiation medium, which is required for osteoblastic differentiation in a two-dimensional cell culture model (165,166).

MTA exhibits minimal cytotoxicity to the human osteoblast MG-63 cell line (167). MTA promotes viability and increases mRNA expression levels of COL1 and OCN in MC3T3-E1 cells induced by MTA, accompanied by enhancement of Alizarin Red-S staining and Alp activity, which suggests that MTA promotes bone matrix formation and mineralization of MC3T3-E1 cells (168-171). Moreover, when incubated on the surface of set MTA, a thick mineralized matrix layer covered with multilayered flat cells is observed in MC3T3-E1 cells after three weeks (169). The mechanism underlying MTA-induced osteoblastic differentiation, mineralization and bone matrix formation in MC3T3-E1 cells in vitro may be associated with the activation of activating transcription factor 6 by MTA and the subsequent endoplasmic reticulum stress response (170). Moreover, Ca, Si and P ions released from MTA (157,172) and alkaline pH value of MTA extract (171) contribute to the bioactivity of MTA. Alkaline pH neutralizes lactic acid, which dissolves mineralization of dentin, and promotes formation of hard tissue by activating alkaline phosphatase (173). MTA with high surface pH exhibits cytotoxicity to MG-63 cells initially (174); the inhibitory effect of MTA on viability of MG-63 cells weakens with the setting of MTA (174), which may be due to the fact that the expression of pro-inflammatory cytokines in MG-63 cells are increased by MTA during the first 24 h but decreased over time (167). Growth factor BMPs promote osteoblastic differentiation and biomineralization (175); the mixture of BMPs and MTA attenuates the cytotoxic effect of MTA to MG-63 cells and inflammation response of tissue to MTA (174). MTA promotes the adhesion, spreading, proliferation and collagen secretion in Saos-2 cells (176,177). Moreover, MTA enhances osteogenic differentiation, Alp activity and calcified nodule formation in Saos-2 cell line (178). By contrast, Modareszadeh et al (179) reported that MTA does not affect survival and Alp activity in Saos-2 cell line. The inconsistency between these studies may due to differences in the preparation of MTA, experimental methods and assessment of Alp activity. Bioaggregate shows no cytotoxicity to MC3T3-E1 and markedly increases expression levels of mineral-associated genes, including COL1, OCN and OPN, in MC3T3-E1 cells compared with MTA (180).

Compared with MTA, Biodentine displays good cytocompatibility with primary human osteoblasts, indicated by enhancement of cell viability, attachment and proliferation (164,181). Similar biocompatibility of MTA and Biodentine has been observed with human osteoblast-like cell line MG63; both enhance viability, adhesion and proliferation of MG63 cells, which may be because Biodentine and MTA have similar surface roughness, heterogeneous morphology and particle size (182). Biodentine and MTA both exhibit positive effects on viability and calcification of MC3T3-E1 cells (183). Biodentine and MTA show dose-dependent effects on viability of Saos-2 cells. Biodentine or MTA at lower concentrations (1:4 and 1:8) result in higher viability of Saos-2 cells. Furthermore, Biodentine stimulates proliferation and migration of Saos-2 cells and induces expression of ALP and mineralization (184).

Compared with MTA, iRoot BP Plus induces greater cytotoxicity to primary human osteoblasts but is still considered as biocompatible because cell viability in the presence of iRoot BP Plus remained >70% compared with that in the control group (185). When MTA or iRoot BP Plus is applied in acidic pH conditions, the secretion of Ca and Si ions is enhanced and apatite formation is decreased. However, cell attachment of MC3T3-E1 on these bioceramics is not affected significantly in an acidic environment. Furthermore, MTA decreases viability, whereas iRoot BP Plus increases survival of MC3T3-E1 cells, which suggests that, compared with MTA, iRoot BP Plus may be more suitable as root-end filling material under inflammatory acidic conditions when used in endodontics (186). By contrast, iRoot FS exhibits better biocompatibility with human osteoblast-like MC3T3-E1 and MG63 cells by promoting their attachment and proliferation (187,186). iRoot FS shows better biocompatibility than MTA or iRoot BP Plus because certain toxic metal substances, such as bismuth (189), aluminium and manganese, are excluded in iRoot FS to enhance its compatibility. On the other hand, smaller particle size on the surface of iRoot FS results in higher cell attachment and subsequent proliferation (188). iRoot SP is non-cytotoxic to MG63 cells and enhances osteoblastic differentiation, which is beneficial to healing inflammatory periapical tissue (190).

Osteoclasts

The migration and fusion of osteoclast precursors is key to osteoclast formation. MTA and Bioaggregate inhibit bone resorption and osteoclast differentiation via preventing the migration and fusion of osteoclast precursors, including mouse bone marrow macrophages (191) and RAW264.7 macrophages (192-194). In addition, MTA inhibits osteoclastogenesis in a dose-dependent manner in the co-culture of mouse bone marrow cells with primary osteoblast cells. Furthermore, MTA suppresses expression of osteoprotegerin in primary osteoblast cells without affecting receptor activator of NF-κB ligand (RANKL) expression levels (195,196). Moreover, MTA solution at low concentration (20%) impairs phosphorylation of c-Src, decreases expression levels of genes encoding MMP-9 and cathepsin K and disrupt formation of actin rings. MTA solution at high concentration (50%) upregulate expression levels of Bim to increase apoptosis of osteoclasts (196). The mechanism underlying MTA-induced inhibition of osteoclastogenesis is associated with attenuation of the autophagic pathway, as demonstrated by decrease in autophagic vacuole and expression levels of autophagic genes and proteins (194). Bioaggregate inhibits osteoclastogenesis via the NF-κB/RANK signaling pathway by decreasing expression levels of Rank, TNF receptor-associated factor 6, NF-κB and nuclear factor of activated T cells 1 (192,193). Bioaggregate and MTA possess comparable ability to decrease osteoclast numbers and attenuate bone resorption (191). Bioaggregate or MTA inhibit osteoclast differentiation and bone resorption due to activation of autophagy in osteoclast differentiation; MTA inhibits osteoclast differentiation via inhibition of the autophagic pathway (194). Compared with MTA, Biodentine exhibits a lower inhibitory effect on osteoclast differentiation and activity of murine bone marrow macrophages by inhibiting ERK1/2 and NF-κB signaling pathways (197). Moreover, the inhibitory effect on osteoclast differentiation and activity of both MTA and Biodentine is similar to that of alendronate, which has been reported to prevent root resorption by inhibiting macrophages (197), which suggests the application of calcium silicate-based bioceramics as treatment to prevent root resorption in endodontics (198,199). iRoot SP shows more cytotoxicity to RAW264.7 cells than MTA but possesses a similar ability to inhibit osteoclastogenesis (200). The aforementioned studies suggested that calcium silicate-based bioceramics attenuate osteoclast differentiation and the primary mechanism is associated with their bioactive elements. Bioactive elements contained in these bioceramics, such as Ca, Mg, Si and Sr, enhance osteoblastic differentiation and suppress RANKL-induced osteoclastogenesis (201-204). A significant increase in Si and Sr ions has been observed in extracts of calcium silicate-based bioceramics (192,205). Si ions enhance the viability, adhesion, differentiation, mineralization and angiogenesis of osteoblasts via the Wnt/β-catenin and MAPK signaling pathways (206-210). Meanwhile, the effect of Si ion on surface roughness is characterized by increased adhesion and proliferation of human osteoblast cell lines (211). Furthermore, Si and Sr ions suppress RANKL-mediated osteoclastic differentiation and bone resorption by inhibiting expression levels of cathepsin K, tartrate-resistant acid phosphatase and c-Fos (205,212,213). In addition, Si and Sr ions create alkaline conditions, which neutralize lactic acid from osteoclasts and promotes accumulation of mineralized components of teeth (214,215). Therefore, the bioactive elements exhibit synergistic effects on osteogenesis, osteoclastogenesis and angiogenesis of associated cells in endodontics (216).

4. Dental pulp or periodontal ligament cells/fibroblasts (PDLC/Fs)

Dental pulp or PDLC/Fs are associated with wound healing and tissue regeneration of dental or periapical tissue, respectively (217). When calcium silicate-based bioceramics are used in pulp capping, cells/fibroblasts from dental pulp are involved in interactions between cells and bioceramics. Cells/fibroblasts from periodontal ligament are affected by bioceramics applied in perforation repair or root-end filling. Numerous studies have investigated the effect on biocompatibility and bioactivity of cells/fibroblasts from dental pulp or periodontal ligament.

Dental pulp cells (DPCs)

Compared with SuperEBA and Vitrebond, MTA exhibits decreased suppression of mitochondrial activity in the rat DPC RPC-C2A cell line (218). Furthermore, MTA significantly promotes proliferation, odontogenic differentiation and mineralization of human DPCs but inhibits secretion of lL-1β and IL-6 (219,220). In order to improve the bioactivity potential of MTA, the growth factor FGF-2 has been added to MTA to enhance its effect on proliferation and osteogenic differentiation of human DPCs (221). Set and fresh MTA display similar biocompatibility with human DPCs. In addition, MTA increases expression of the angiogenic factors VEGF and angiogenin (222). In comparison with MTA, Bioaggregate and Biodentine possess equal biocompatibility with human DPCs. Moreover, Bioaggregate, Biodentine and MTA enhance mRNA expression levels of ostogenic/odontogenic genes, such as ALP, OPN, OCN, DSPP and DMP-1, increase Alp activity and promote mineralization nodule formation due to activation of the MAPK signaling pathway induced by these calcium silicate-based bioceramics (223,224). In addition, Bioaggregate exhibits superior capacity to MTA in terms of adhesion, attachment and migration of human DPCs (225). Moreover, compared with MTA, Bioaggregate induces enhanced mineralization and odontoblastic differentiation in human DPCs (226). In terms of osteogenic differentiation of human DPCs, Bioaggregate displays stronger potential than MTA (223). Both Biodentine and MTA promote mineralization by increasing secretion of TGF-β1 from human DPCs, which mediates mineralization-associated cellular activity and subsequent dentin bridge formation (227,228). Biodentine enhances cell proliferation, viability, migration, adhesion, odontoblastic differentiation and biomineralization of the immortalized murine DPC OD-21 cell line (229). iRoot BP Plus exhibits a higher proliferation rate of human DPCs compared with MTA during the whole culture period (230). Moreover, iRoot BP Plus promotes migration and upregulates the expression of focal adhesion molecules in human DPCs via the ERK 1/2, JNK and Akt signaling pathways (231). In addition, iRoot BP Plus possesses stronger potential than MTA to enhance the mineralization and odontoblastic differentiation of human DPCs (226).

Dental pulp fibroblasts (DPFs)

Given that Ca(OH)2 and MTA are used in pulp capping, Kierat et al (232) compared cytotoxicity to human DPFs; MTA was less cytotoxic to human DPFs compared with Ca(OH)2. Likewise, Zakerzadeh et al (233) compared the biocompatibility of MTA and Biodentine with human DPFs; MTA and Biodentine did not display cytotoxicity or genotoxicity at 0-1,000 µg/ml concentration. Similarly, Biodentine does not influence the morphology, proliferation or cell integrity of human DPFs, but affects cell survival in a concentration- and time-dependent manner (234). Moreover, higher concentration of Biodentine suppress differentiation of DPFs by decreasing production of COL1 and TGF-β1 (234), whereas Biodentine at lower concentrations stimulate TGF-β1 secretion (228). Both TGF-β1 and COL1 exhibit notable effects on collagen synthesis, mineralization and hard dental tissue generation (228,235-237). TGF-β1 and FGF-2 are also involved in proliferation, differentiation and migration of DPFs (228,238,239). Giraud et al investigated the effect of Biodentine on injured human DPFs; Biodentine increased cellular survival and migration, as well as the secretion of FGF-2 and TGF-β1 in lipoteichoic acid-stimulated and physically injured human DPFs. Moreover, injured DPFs exhibit decreased levels of pro-inflammatory cytokines, such as IL-6, and inflammatory cell recruitment in the presence of Biodentine compared with that in the presence of resin-containing TheraCal (240). TheraCal inhibits proliferation of human DPFs while Biodentine has no effect on proliferation of human DPFs. In addition, decreased release of pro-inflammatory cytokine IL-8 and higher mineralization have been observed in human DPFs induced by Biodentine compared with TheraCal (78). In addition, complement, particularly the C5a fragment, is involved in initiation of inflammation (241) and recruitment of DPSCs in regeneration (242). Due to the fact that C5a is produced by local DPFs when dental pulp is injured, Giraud et al compared several pulp capping materials and their effect on release of C5a in human DPFs. The results revealed that C5a secretion of injured human DPFs was not affected by Biodentine, whereas TheraCal increased C5a secretion. Furthermore, compared with TheraCal, Biodentine significantly decreased recruitment of THP-1 cells involved in inflammation by affecting C5a/C5a receptor interactions (243). These results suggested that calcium silicate-based Biodentine affects the balance between initial pulp inflammatory reaction and subsequent pulp healing by affecting complement activation following pulp injury. Calcium silicate-based bioceramics shift the balance toward pulp healing, whereas resin-containing materials shift the balance toward pulp inflammation (78,240).

PDLCs

Vidovic Zdrilic et al (111) found that MTA-conditioned medium promotes healing of injured periapical tissue in vivo, whereas MTA inhibits viability and biomineralization in mouse PDLCs in vitro. Eluate extract from MTA results in decreased viability and increased death of human PDLCs compared with those in a control group (medium-only) (244). By contrast, when human PDLCs are incubated with set MTA, MTA enhances mineralization and BMP-2 expression levels, which is caused by gradual production of Ca2+ from MTA and the interaction of BMP2/BMP-2 receptors in human PDLCs (245). These contradictory results may be due to different preparation methods of MTA. Set MTA releases calcium gradually and calcium at low concentrations stimulates cells mildly, whereas MTA-conditioned medium leads to immediate release of calcium at high concentrations; this may exert a negative effect on bioactivity of MTA to PDLCs. Compared with MTA, Bioaggregate displays better biocompatibility with human PDLCs, which may be due to the absence of aluminium in Bioaggregate. Moreover, the primary components of Bioaggregate, calcium silicate, calcium hydroxide and hydroxyapatite, stimulate proliferation of human PDLCs (246). In addition, Bioaggregate significantly increases mineralization in PDLCs in a concentration- and time-dependent manner. Furthermore, Bioaggregate enhances differentiation of PDLCs, particularly osteogenic differentiation, via microRNA-146a upregulation, as demonstrated by increased expression levels of ALP, DMP1 and BMP and decreased cementum protein 1 expression levels in PDLCs (247). In comparison with MTA, Biodentine exhibits equally good biocompatibility with human PDLCs (55,181). Moreover, Biodentine displays greater potential in terms of attachment and proliferation of human PDLCs compared with MTA, which may be due to its hydroxyl apatite-like surface characteristics and greater release of calcium and silicon ions compared with MTA (181). Luo et al compared bioactivity of Biodentine and iRoot FS to human PDLCs and showed that both Biodentine and iRoot FS increased the adhesion of human PDLCs. iRoot FS possesses superior ability to Biodentine to promote viability, proliferation and osteoblastic differentiation of human PDLCs (248). In order to clarify the bioactivity of iRoot SP to human PDLCs, Chang et al investigated the biocompatibility and bioactivity of four root canal sealers: iRoot SP, Sealapex (Kerr Corporation), ARS (Dentsply-Sankin KK) and MTA Fillapex. The results revealed that all sealers were non-toxic to human PDLCs and increased Alp activity and formation of mineralization nodules. However, compared with Sealapex, an epoxy resin-based material, the other three sealers induced lower inflammatory response and enhanced osteogenic differentiation in PDLCs via the integrin-mediated signaling pathway (249).

PDLFs

Human PDLFs exhibit decreased proliferation rate when cultured on the surface of MTA compared with culturing on the surface of a coverslip (250); PDLFs on the surface of MTA have a rounded morphology with blunted extensions, while PDLFs on the surface of glass coverslips show good attachment and spreading (251). Balto investigated the effect of MTA surface characteristics on attachment of human PDLFs; human PDLFs did not attach to fresh MTA and the surface of cells appeared less smooth and exhibited more vacuoles. By contrast, human PDLFs on the surface of set MTA were round and flattened with smooth surfaces and attached well to MTA (252). Similarly, Bonson et al reported that human PDLFs exposed to washed MTA possess greater proliferation capacity those exposed to fresh MTA. Moreover, compared with fresh MTA, washed MTA exhibits stronger potential to induce osteogenic differentiation of human PDLFs (253). Compared with other endodontic materials, such as Diaket (ESPE; 3M), Super-EBA (Harry J Bosworth Company) and amalgam, MTA also displays better biocompatibility with human PDLFs and does not induce apoptosis and necrosis of human PDLFs (254-257). Compared with these other materials in root perforation models in vitro, MTA also results in higher viability in human PDLFs and induces mRNA expression levels of COL1 and RUNX2 in human PDLFs, which suggests that MTA has potential to induce osteogenic differentiation of PDLFs, which is key for periodontal regeneration (105). Likewise, MTA-conditioned medium at low concentrations (0.5, 5.0 and 50.0 µg/ml) possesses superior capacity to formocresol and ferric sulphate in maintaining the viability of human PDLFs, whereas MTA at higher concentrations (5,000 µg/ml) shows slight cytotoxicity to human PDLFs (258,259). Bioaggregate displays biocompatibility with human PDLFs comparable to that of MTA, whereas viability of human PDLFs in the presence of Biodentine is slightly decreased compared with MTA (260-262). By contrast, Akbulut et al (263) reported that Biodentine possesses better biocompatibility with human PDLFs. This discrepancy may be associated with chemical composition of the material, assessment time point and surface characteristics. In terms of chemical composition, calcium chloride used in the liquid of Biodentine as an accelerator decreases the setting time (264) and results in early production of calcium hydroxide, which contributes to relatively decreased cell survival after 24 h in the presence of Biodentine (265). Moreover, zirconium oxide in Biodentine is non-toxic to murine PDLFs, but bismuth oxide in MTA has no impact on cell growth (266). MTA supports higher cell viability during the first 24 h but decreases cell viability to 80% later (251,260). Biodentine maintains lower cell viability during the first 24 h but viability increases gradually over time (261). Human PDLFs attach well to the surfaces of both MTA and Biodentine and maintain their original morphology. Nevertheless, more cell aggregates have been observed on the surface of Biodentine, whereas human PDLFs tend to show greater spread and elongation on MTA (267). Moreover, expression levels of Integrin β1 and Vinculin, which are associated with focal contacts between human PDLFs and bioceramics, are higher in human PDLFs treated with Biodentine than in those treated with MTA, which suggests that the surface characteristics of Biodentine promote the adhesion and survival of human PDLFs more strongly compared with MTA (268).

5. Immune cells

Immune cells, such as monocytes and macrophages, respond immediately when biomaterials are placed into tissue, which causes the initial inflammatory response and tissue healing. Macrophages release pro-inflammatory cytokines in the beginning of an acute inflammatory response, such as TNF-α, IL-1 and IL-12, but release anti-inflammatory cytokines during regeneration and healing of tissue, such as IL-4, which contributes to the production of fibronectin (269-271). MTA displays detectable, but not statistically significant, cytotoxicity to human monocytic cell line THP1 and alters secretion of inflammatory cytokines (272). In addition, macrophages and mast cells participate in leukocyte recruitment and extravasation via secretion of inflammatory cytokines that regulate inflammation control and tissue healing in pulpitis and apical periodontitis (273,274). Moreover, neutrophil chemotactic factor is induced from macrophages and mast cells by MTA; the upregulation of these neutrophil chemotactic factor substances participates in migration and accumulation of neutrophils, monocytes and lymphocytes (275-277). Similarly, Cavalcanti et al (278) found that MTA increases secretion of IL-8 and IL-1β, which supports the migration of human neutrophils. Chang et al (279) discovered that MTA enhances migration of immune cells, which is regulated by calcium-sensing receptors and the PI3K pathway for chemotaxis, as well as the Ca2+-calmodulin-dependent MLCK pathway for chemokinesis.

M1/M2 macrophage polarization is associated with the inflammatory response and subsequent tissue regeneration following biomaterial implantation (270,280,281). Tu et al found that iRoot SP induces greater cytotoxicity to RAW264.7 macrophages than MTA. Furthermore, both MTA and iRoot SP induce expression of pro-inflammatory cytokines without inducing osteoclastogenesis in RAW264.7 macrophages. In addition, MTA primarily induces M2 macrophage polarization, whereas iRoot SP induces M1 macrophage polarization (200). Both MTA and iRoot SP are non-toxic to RAW264.7 cells (282). Moreover, MTA does not affect the viability and adherence of M1 and M2 macrophages isolated from mice (283,284). MTA and iRoot SP reinforce expression of inflammatory cytokines in RAW264.7 cells. Furthermore, MTA and iRoot SP possess equal capacity to stimulate M1/M2 macrophage polarization but greater M2 macrophage polarization is induced, which implies that calcium silicate-based bioceramics shift M1/M2 polarization balance to M2 macrophage polarization under inflammatory conditions (282,285). Yeh et al reported that MTA induces THP-1 cells toward M2 polarization by activating the Axl/Akt/NF-κB signaling pathway. MTA promotes tissue regeneration and wound healing via M2 macrophage polarization (286). MTA does not induce DNA breakage of human peripheral lymphocytes, which is the first step in carcinogenesis. This suggests that MTA exhibits no potential carcinogenic risk when used in endodontics (287).

Compared with other pulp capping materials, such as TheraCal and Xeno III, Biodentine decreases migration and adhesion of THP-1 cells to endothelial cells and inhibits their activation to macrophages in vitro (240). In addition, Biodentine does not stimulate expression of inflammation-associated enzymes in vitro, such as prostaglandin E2 and thromboxane (288). Compared with MTA, Biodentine displays a more notable inhibitory effect on mRNA and protein expression levels of inflammatory cytokines in RAW264.7 macrophages (183). Biodentine is biocompatible with immune cells, which is consistent with another study that demonstrated that Biodentine exhibits similar biocompatibility with human monocytes compared with MTA (289).

6. Conclusion

There have been numerous studies on the in vitro biocompatibility and bioactivity of calcium silicate-based bioceramics in endodontics (16,79,147,192). MTA has been investigated most thoroughly and is considered the gold standard. However, compared with MTA, there are not enough studies to assess the biocompatibility and bioactivity of other calcium silicate-based bioceramics, such as Bioaggregate, Biodentine and iRoot BP/FS/SP, in endodontics. Therefore, further studies are required. Results from various in vitro models are inconsistent due to several reasons. Considering the discrepancy in cell types and methods to prepare the sample and evaluate the effect of MTA, it is difficult to compare the results and conclusions from different studies. Firstly, (patho-) physiological and anatomical differences between cells may lead to discrepancies in results. Secondly, experimental procedures and associated assessment criteria are distinctive so it is difficult to compare results directly and apply them to use in humans. It is essential to establish a well-defined gold standard model, experimental procedures and evaluation criteria to overcome this. Although calcium silicate-based bioceramics display excellent biocompatibility and bioactivity, the combined use of calcium silicate-based bioceramics with other materials/procedures improves efficiency of the calcium silicate-based bioceramics in endodontics. For example, the addition of TGF-β1 and VEGF to bioceramics displays better biocompatibility with human DPSCs and promotes formation of dentin bridge in rat pulp capping compared with MTA (290). Further studies are required to determine the effects of combined bioceramics.

Availability of data and materials

Not applicable.

Authors' contributions

WS conceived and wrote the manuscript. WS and SL contributed to data acquisition, analysis and interpretation. QT made substantial contributions to conception and design. LC and ZY critically revised the manuscript. Data sharing is not applicable. All authors read and approved the final manuscript.

Ethics approval and consent to participate

Not applicable.

Patient consent for publication

Not applicable.

Competing interests

The authors declare they have no competing interests.

Acknowledgments

Not applicable.

Funding

The present review was supported by grants from the National Key R&D Program of China (grant no. 2017YFC1104301) and National Natural Science Foundation of China (grant no. 81700955).

References

1 

Liu H, Gronthos S and Shi S: Dental pulp stem cells. Methods Enzymol. 419:99–113. 2006. View Article : Google Scholar : PubMed/NCBI

2 

Heyeraas KJ and Kvinnsland I: Tissue pressure and blood flow in pulpal inflammation. Proc Finn Dent Soc. 88(Suppl 1): S393–S401. 1992.

3 

Mohammadi Z and Dummer PMH: Properties and applications of calcium hydroxide in endodontics and dental traumatology. Int Endod J. 44:697–730. 2011. View Article : Google Scholar : PubMed/NCBI

4 

Siew K, Lee AH and Cheung GS: Treatment outcome of repaired root perforation: A systematic review and meta-analysis. J Endod. 41:1795–1804. 2015. View Article : Google Scholar : PubMed/NCBI

5 

Juneja P and Kulkarni S: Clinical and radiographic comparison of biodentine, mineral trioxide aggregate and formocresol as pulpotomy agents in primary molars. Eur Arch Paediatr Dent. 18:271–278. 2017. View Article : Google Scholar : PubMed/NCBI

6 

Suhag K, Duhan J, Tewari S and Sangwan P: Success of direct pulp capping using mineral trioxide aggregate and calcium hydroxide in mature permanent molars with pulps exposed during carious tissue removal: 1-year follow-up. J Endod. 45:840–847. 2019. View Article : Google Scholar : PubMed/NCBI

7 

Gutmann JL and Pitt Ford TR: Management of the resected root end: A clinical review. Int Endod J. 26:273–283. 1993. View Article : Google Scholar : PubMed/NCBI

8 

Abusrewil SM, McLean W and Scott JA: The use of Bioceramics as root-end filling materials in periradicular surgery: A literature review. Saudi Dent J. 30:273–282. 2018. View Article : Google Scholar : PubMed/NCBI

9 

Torabinejad M, Watson TF and Pitt Ford TR: Sealing ability of a mineral trioxide aggregate when used as a root end filling material. J Endod. 19:591–595. 1993. View Article : Google Scholar : PubMed/NCBI

10 

Asgary S, Eghbal MJ and Parirokh M: Sealing ability of a novel endodontic cement as a root-end filling material. J Biomed Mater Res A. 87:706–709. 2008. View Article : Google Scholar : PubMed/NCBI

11 

Parirokh M, Torabinejad M and Dummer PMH: Mineral trioxide aggregate and other bioactive endodontic cements: An updated overview-part I: Vital pulp therapy. Int Endod J. 51:177–205. 2018. View Article : Google Scholar

12 

Torabinejad M, Parirokh M and Dummer P: Mineral trioxide aggregate and other bioactive endodontic cements: An updated overview part II: Other clinical applications and complications. Int Endod J. 51:284–317. 2018. View Article : Google Scholar

13 

Majeed A and AlShwaimi E: Push-out bond strength and surface microhardness of calcium silicate-based biomaterials: An in vitro study. Med Princ Pract. 26:139–145. 2017. View Article : Google Scholar :

14 

Song W, Sun W, Chen L and Yuan Z: In vivo biocompatibility and bioactivity of calcium silicate-based bioceramics in endodontics. Front Bioeng Biotechnol. 8:5809542020. View Article : Google Scholar :

15 

Rodriguez-Lozano FJ, Lopez-Garcia S, Garcia-Bernal D, Sanz JL, Lozano A, Pecci-Lloret MP, Melo M, Lopez-Gines C and Forner L: Cytocompatibility and bioactive properties of the new dual-curing resin-modified calcium silicate-based material for vital pulp therapy. Clin Oral Investig. Feb 27–2021.Epub ahead of print. View Article : Google Scholar : PubMed/NCBI

16 

Garrido M, Morales D, Saldias MP, Fernandez C, Villalobos V, Cerda O and Caceres M: Cellular response of human apical papilla cells to calcium hydroxide and tricalcium silicate-based cements. BMC Oral Health. 21:1062021. View Article : Google Scholar : PubMed/NCBI

17 

Lemons JE: Ceramics: Past, present, and future. Bone. 19(Suppl 1): 121S–128S. 1996. View Article : Google Scholar : PubMed/NCBI

18 

Hench LL and Wilson J: Surface-active biomaterials. Science. 226:630–636. 1984. View Article : Google Scholar : PubMed/NCBI

19 

Grech L, Mallia B and Camilleri J: Investigation of the physical properties of tricalcium silicate cement-based root-end filling materials. Dent Mater. 29:e20–e28. 2013. View Article : Google Scholar

20 

Shokouhinejad N, Nekoofar MH, Razmi H, Sajadi S, Davies TE, Saghiri MA, Gorjestani H and Dummer PM: Bioactivity of EndoSequence root repair material and bioaggregate. Int Endod J. 45:1127–1134. 2012. View Article : Google Scholar : PubMed/NCBI

21 

Han L, Okiji T and Okawa S: Morphological and chemical analysis of different precipitates on mineral trioxide aggregate immersed in different fluids. Dent Mater J. 29:512–517. 2010. View Article : Google Scholar : PubMed/NCBI

22 

Camilleri J: Characterization and hydration kinetics of tricalcium silicate cement for use as a dental biomaterial. Dent Mater. 27:836–844. 2011. View Article : Google Scholar : PubMed/NCBI

23 

Zhao W, Chang J and Zhai W: Self-setting properties and in vitro bioactivity of Ca3SiO5/CaSO4.1/2H2O composite cement. J Biomed Mater Res A. 85:336–344. 2008. View Article : Google Scholar

24 

Zhao W, Wang J, Zhai W, Wang Z and Chang J: The self-setting properties and in vitro bioactivity of tricalcium silicate. Biomaterials. 26:6113–6121. 2005. View Article : Google Scholar : PubMed/NCBI

25 

Chen I, Salhab I, Setzer FC, Kim S and Nah HD: A new calcium silicate-based bioceramic material promotes human osteo- and odontogenic stem cell proliferation and survival via the extracellular signal-regulated kinase signaling pathway. J Endod. 42:480–486. 2016. View Article : Google Scholar : PubMed/NCBI

26 

Morsczeck C and Reichert TE: Dental stem cells in tooth regeneration and repair in the future. Expert Opin Biol Ther. 18:187–196. 2018. View Article : Google Scholar

27 

Aydin S and Sahin F: Stem cells derived from dental tissues. Adv Exp Med Biol. 1144:123–132. 2019. View Article : Google Scholar : PubMed/NCBI

28 

Rodriguez-Lozano FJ, Bueno C, Insausti CL, Meseguer L, Ramirez MC, Blanquer M, Marin N, Martinez S and Moraleda JM: Mesenchymal stem cells derived from dental tissues. Int Endod J. 44:800–806. 2011. View Article : Google Scholar : PubMed/NCBI

29 

Rombouts C, Giraud T, Jeanneau C and About I: Pulp Vascularization during tooth development, regeneration, and therapy. J Dent Res. 96:137–144. 2017. View Article : Google Scholar : PubMed/NCBI

30 

Murray PE, Garcia-Godoy F and Hargreaves KM: Regenerative endodontics: A review of current status and a call for action. J Endodont. 33:377–390. 2007. View Article : Google Scholar

31 

Orti V, Collart-Dutilleul PY, Piglionico S, Pall O, Cuisinier F and Panayotov I: Pulp regeneration concepts for nonvital teeth: From tissue engineering to clinical approaches. Tissue Eng Part B Rev. 24:419–442. 2018. View Article : Google Scholar : PubMed/NCBI

32 

Sugawara Y, Suzuki K, Koshikawa M, Ando M and Iida J: Necessity of enzymatic activity of alkaline phosphatase for mineralization of osteoblastic cells. Jpn J Pharmacol. 88:262–269. 2002. View Article : Google Scholar : PubMed/NCBI

33 

Cormier C: Markers of bone metabolism. Curr Opin Rheumatol. 7:243–248. 1995. View Article : Google Scholar : PubMed/NCBI

34 

Rodan GA and Noda M: Gene expression in osteoblastic cells. Crit Rev Eukaryot Gene Expr. 1:85–98. 1991.PubMed/NCBI

35 

Camilleri S and McDonald F: Runx2 and dental development. Eur J Oral Sci. 114:361–373. 2006. View Article : Google Scholar : PubMed/NCBI

36 

Karsenty G and Wagner EF: Reaching a genetic and molecular understanding of skeletal development. Dev Cell. 2:389–406. 2002. View Article : Google Scholar : PubMed/NCBI

37 

Rathinam E, Rajasekharan S, Chitturi RT, Martens L and De Coster P: Gene expression profiling and molecular signaling of dental pulp cells in response to tricalcium silicate cements: A systematic review. J Endod. 41:1805–1817. 2015. View Article : Google Scholar : PubMed/NCBI

38 

Bai Y, Bai Y, Matsuzaka K, Hashimoto S, Kokubu E, Wang X and Inoue T: Formation of bone-like tissue by dental follicle cells co-cultured with dental papilla cells. Cell Tissue Res. 342:221–231. 2010. View Article : Google Scholar : PubMed/NCBI

39 

Gibson MP, Zhu Q, Wang S, Liu Q, Liu Y, Wang X, Yuan B, Ruest LB, Feng JQ, D'Souza RN, et al: The rescue of dentin matrix protein 1 (DMP1)-deficient tooth defects by the transgenic expression of dentin sialophosphoprotein (DSPP) indicates that DSPP is a downstream effector molecule of DMP1 in dentinogenesis. J Biol Chem. 288:7204–7214. 2013. View Article : Google Scholar : PubMed/NCBI

40 

Lee SK, Lee KE, Jeon D, Lee G, Lee H, Shin CU, Jung YJ, Lee SH, Hahn SH and Kim JW: A novel mutation in the DSPP gene associated with dentinogenesis imperfecta type II. J Dent Res. 88:51–55. 2009. View Article : Google Scholar : PubMed/NCBI

41 

Chang CC, Yeh CL, Chang HH, Kuo YF, Huang PY and Lin CP: Effect of different zinc concentrations on partially-stabilized cement for vital pulp therapy. J Formos Med Assoc. 118:1610–1615. 2019. View Article : Google Scholar : PubMed/NCBI

42 

Zhao X, He W, Song Z, Tong Z, Li S and Ni L: Mineral trioxide aggregate promotes odontoblastic differentiation via mitogen-activated protein kinase pathway in human dental pulp stem cells. Mol Biol Rep. 39:215–220. 2012. View Article : Google Scholar

43 

Tomas-Catala CJ, Collado-Gonzalez M, Garcia-Bernal D, Onate-Sanchez RE, Forner L, Llena C, Lozano A, Castelo-Baz P, Moraleda JM and Rodriguez-Lozano FJ: Comparative analysis of the biological effects of the endodontic bioactive cements MTA-Angelus, MTA Repair HP and NeoMTA Plus on human dental pulp stem cells. Int Endod J. 50(Suppl 2): e63–e72. 2017. View Article : Google Scholar : PubMed/NCBI

44 

Wang Y, Yan M, Fan Z, Ma L, Yu Y and Yu J: Mineral trioxide aggregate enhances the odonto/osteogenic capacity of stem cells from inflammatory dental pulps via NF-κB pathway. Oral Dis. 20:650–658. 2014. View Article : Google Scholar

45 

Jaberiansari Z, Naderi S and Tabatabaei FS: Cytotoxic effects of various mineral trioxide aggregate formulations, calcium-enriched mixture and a new cement on human pulp stem cells. Iran Endod J. 9:271–276. 2014.PubMed/NCBI

46 

Niu LN, Watson D, Thames K, Primus CM, Bergeron BE, Jiao K, Bortoluzzi EA, Cutler CW, Chen JH, Pashley DH and Tay FR: Effects of a discoloration-resistant calcium aluminosilicate cement on the viability and proliferation of undifferentiated human dental pulp stem cells. Sci Rep. 5:171772015. View Article : Google Scholar : PubMed/NCBI

47 

Mohamed DA, Abdelfattah MI and Aboulezz EH: The effect of three different biomaterials on proliferation and viability of human dental pulp stem cells (In-vitro Study). Open Access Maced J Med Sci. 5:657–663. 2017. View Article : Google Scholar : PubMed/NCBI

48 

Kulan P, Karabiyik O, Kose GT and Kargul B: The effect of accelerated mineral trioxide aggregate on odontoblastic differentiation in dental pulp stem cell niches. Int Endod J. 51:758–766. 2018. View Article : Google Scholar

49 

Youssef AR, Emara R, Taher MM, Al-Allaf FA, Almalki M, Almasri MA and Siddiqui SS: Effects of mineral trioxide aggregate, calcium hydroxide, biodentine and Emdogain on osteogenesis, Odontogenesis, angiogenesis and cell viability of dental pulp stem cells. BMC Oral Health. 19:1332019. View Article : Google Scholar : PubMed/NCBI

50 

Minyong W, He L, Shenglin L and Man Q: Effects of mineral trioxide aggregate on the proliferation and differentiation of human pulp cells from primary and permanent teeth. Hua Xi Kou Qiang Yi Xue Za Zhi. 33:75–79. 2015.In Chinese. PubMed/NCBI

51 

Camilleri J, Montesin FE, Papaioannou S, McDonald F and Pitt Ford TR: Biocompatibility of two commercial forms of mineral trioxide aggregate. Int Endod J. 37:699–704. 2004. View Article : Google Scholar : PubMed/NCBI

52 

Demirkaya K, Can Demirdöğen B, Öncel Torun Z, Erdem O, Cetinkaya S and Akay C: In vivo evaluation of the effects of hydraulic calcium silicate dental cements on plasma and liver aluminium levels in rats. Eur J Oral Sci. 124:75–81. 2016. View Article : Google Scholar

53 

Chung M, Lee S, Chen D, Kim U, Kim Y, Kim S and Kim E: Effects of different calcium silicate cements on the inflammatory response and odontogenic differentiation of lipopolysaccharide-stimulated human dental pulp stem cells. Materials (Basel). 12:12592019. View Article : Google Scholar

54 

Chen M, Hu DN, Pan Z, Lu CW, Xue CY and Aass I: Curcumin protects against hyperosmoticity-induced IL-1beta elevation in human corneal epithelial cell via MAPK pathways. Exp Eye Res. 90:437–443. 2010. View Article : Google Scholar

55 

Tang JJ, Shen ZS, Qin W and Lin Z: A comparison of the sealing abilities between Biodentine and MTA as root-end filling materials and their effects on bone healing in dogs after periradicular surgery. J Appl Oral Sci. 27:e201806932019. View Article : Google Scholar : PubMed/NCBI

56 

Zhang W and Peng B: Tissue reactions after subcutaneous and intraosseous implantation of iRoot SP, MTA and AH Plus. Dent Mater J. 34:774–780. 2015. View Article : Google Scholar : PubMed/NCBI

57 

Masuda-Murakami Y, Kobayashi M, Wang X, Yamada Y, Kimura Y, Hossain M and Matsumoto K: Effects of mineral trioxide aggregate on the differentiation of rat dental pulp cells. Acta Histochem. 112:452–458. 2010. View Article : Google Scholar

58 

Agrafioti A, Taraslia V, Chrepa V, Lymperi S, Panopoulos P, Anastasiadou E and Kontakiotis EG: Interaction of dental pulp stem cells with Biodentine and MTA after exposure to different environments. J Appl Oral Sci. 24:481–486. 2016. View Article : Google Scholar : PubMed/NCBI

59 

Utneja S, Nawal RR, Talwar S and Verma M: Current perspectives of bio-ceramic technology in endodontics: Calcium enriched mixture cement-review of its composition, properties and applications. Restor Dent Endod. 40:1–13. 2015. View Article : Google Scholar : PubMed/NCBI

60 

Bin CV, Valera MC, Camargo SE, Rabelo SB, Silva GO, Balducci I and Camargo CH: Cytotoxicity and genotoxicity of root canal sealers based on mineral trioxide aggregate. J Endod. 38:495–500. 2012. View Article : Google Scholar : PubMed/NCBI

61 

Liu X, Zhao M, Lu J, Ma J, Wei J and Wei S: Cell responses to two kinds of nanohydroxyapatite with different sizes and crystallinities. Int J Nanomedicine. 7:1239–1250. 2012. View Article : Google Scholar : PubMed/NCBI

62 

Hanafy AK, Shinaishin SF, Eldeen GN and Aly RM: Nano Hydroxyapatite & mineral trioxide aggregate efficiently promote odontogenic differentiation of dental pulp stem cells. Open Access Maced J Med Sci. 6:1727–1731. 2018. View Article : Google Scholar : PubMed/NCBI

63 

Paranjpe A, Zhang H and Johnson JD: Effects of mineral trioxide aggregate on human dental pulp cells after pulp-capping procedures. J Endod. 36:1042–1047. 2010. View Article : Google Scholar : PubMed/NCBI

64 

Seo MS, Hwang KG, Lee J, Kim H and Baek SH: The effect of mineral trioxide aggregate on odontogenic differentiation in dental pulp stem cells. J Endod. 39:242–248. 2013. View Article : Google Scholar : PubMed/NCBI

65 

Okamoto M, Ali M, Komichi S, Watanabe M, Huang H, Ito Y, Miura J, Hirose Y, Mizuhira M, Takahashi Y, et al: Surface pre-reacted glass filler contributes to tertiary dentin formation through a mechanism different than that of hydraulic calcium-silicate cement. J Clin Med. 8:14402019. View Article : Google Scholar :

66 

Asgary S, Nazarian H, Khojasteh A and Shokouhinejad N: Gene expression and cytokine release during odontogenic differentiation of human dental pulp stem cells induced by 2 endodontic biomaterials. J Endod. 40:387–392. 2014. View Article : Google Scholar : PubMed/NCBI

67 

Paranjpe A, Cacalano NA, Hume WR and Jewett A: N-acetylcysteine protects dental pulp stromal cells from HEMA-induced apoptosis by inducing differentiation of the cells. Free Radic Biol Med. 43:1394–1408. 2007. View Article : Google Scholar : PubMed/NCBI

68 

Caicedo R, Abbott PV, Alongi DJ and Alarcon MY: Clinical, radiographic and histological analysis of the effects of mineral trioxide aggregate used in direct pulp capping and pulpotomies of primary teeth. Aust Dent J. 51:297–305. 2006. View Article : Google Scholar

69 

Maroto M, Barberia E, Planells P and García Godoy F: Dentin bridge formation after mineral trioxide aggregate (MTA) pulpotomies in primary teeth. Am J Dent. 18:151–154. 2005.PubMed/NCBI

70 

Javid B, Panahandeh N, Torabzadeh H, Nazarian H, Parhizkar A and Asgary S: Bioactivity of endodontic biomaterials on dental pulp stem cells through dentin. Restor Dent Endod. 45:e32019. View Article : Google Scholar

71 

Kulan P, Karabiyik O, Kose GT and Kargul B: Biocompatibility of accelerated mineral trioxide aggregate on stem cells derived from human dental pulp. J Endod. 42:276–279. 2016. View Article : Google Scholar

72 

Kim JH, Kim SY, Woo SM, Jeong HN, Jung JY, Kim SM and Lim HS: Combination of mineral trioxide aggregate and propolis promotes odontoblastic differentiation of human dental pulp stem cells through ERK signaling pathway. Food Sci Biotechnol. 28:1801–1809. 2019. View Article : Google Scholar : PubMed/NCBI

73 

Olcay K, Tasli PN, Guven EP, Ulker G, Ogut EE, Ciftcioglu E, Kiratli B and Sahin F: Effect of a novel bioceramic root canal sealer on the angiogenesis-enhancing potential of assorted human odontogenic stem cells compared with principal tricalcium silicate-based cements. J Appl Oral Sci. 28:e201902152020. View Article : Google Scholar : PubMed/NCBI

74 

Tomas-Catala CJ, Collado-Gonzalez M, Garcia-Bernal D, Onate-Sanchez RE, Forner L, Llena C, Lozano A, Moraleda JM and Rodriguez-Lozano FJ: Biocompatibility of New Pulp-capping Materials NeoMTA Plus, MTA Repair HP, and biodentine on human dental pulp stem cells. J Endod. 44:126–132. 2018. View Article : Google Scholar

75 

Luo Z, Li D, Kohli MR, Yu Q, Kim S and He WX: Effect of Biodentine™ on the proliferation, migration and adhesion of human dental pulp stem cells. J Dent. 42:490–497. 2014. View Article : Google Scholar : PubMed/NCBI

76 

Luo Z, Kohli MR, Yu Q, Kim S, Qu T and He WX: Biodentine induces human dental pulp stem cell differentiation through mitogen-activated protein kinase and calcium-/calmodulin-dependent protein kinase II pathways. J Endod. 40:937–942. 2014. View Article : Google Scholar : PubMed/NCBI

77 

Bortoluzzi EA, Niu LN, Palani CD, El-Awady AR, Hammond BD, Pei DD, Tian FC, Cutler CW, Pashley DH and Tay FR: Cytotoxicity and osteogenic potential of silicate calcium cements as potential protective materials for pulpal revascularization. Dent Mater. 31:1510–1522. 2015. View Article : Google Scholar : PubMed/NCBI

78 

Jeanneau C, Laurent P, Rombouts C, Giraud T and About I: Light-cured tricalcium silicate toxicity to the dental pulp. J Endod. 43:2074–2080. 2017. View Article : Google Scholar : PubMed/NCBI

79 

Weekate K, Chuenjitkuntaworn B, Chuveera P, Vaseenon S, Chompu-Inwai P, Ittichaicharoen J, Chattipakorn S and Srisuwan T: Alterations of mitochondrial dynamics, inflammation and mineralization potential of lipopolysaccharide-induced human dental pulp cells after exposure to N-acetyl cysteine, Biodentine or ProRoot MTA. Int Endod J. Jan 27–2021.Epub ahead of print. View Article : Google Scholar : PubMed/NCBI

80 

Loison-Robert LS, Tassin M, Bonte E, Berbar T, Isaac J, Berdal A, Simon S and Fournier BPJ: In vitro effects of two silicate-based materials, Biodentine and BioRoot RCS, on dental pulp stem cells in models of reactionary and reparative dentinogenesis. PLoS One. 13:e1900142018. View Article : Google Scholar

81 

Kuru S, Sepet E, Irez T, Aktas E, Yazir Y, Duruksu G, Osmanoglu Akyol E and Erguven M: Effects of different pulp-capping materials on cell death signaling pathways of lipoteichoic acid-stimulated human dental pulp stem cells. Odontology. 109:547–559. 2021. View Article : Google Scholar

82 

Petta TM, Pedroni ACF, Saavedra DF, Faial KDCF, Marques MM and Couto RSD: The effect of three different pulp capping cements on mineralization of dental pulp stem cells. Dent Mater J. 39:222–228. 2020. View Article : Google Scholar

83 

Tsujimoto M, Ookubo A, Wada Y, Matsunaga T, Tsujimoto Y and Hayashi Y: Surface changes of mineral trioxide aggregate after the application of bleaching agents: Electron microscopy and an energy-dispersive X-ray microanalysis. J Endod. 37:231–234. 2011. View Article : Google Scholar : PubMed/NCBI

84 

Namazikhah MS, Nekoofar MH, Sheykhrezae MS, Salariyeh S, Hayes SJ, Bryant ST, Mohammadi MM and Dummer PM: The effect of pH on surface hardness and microstructure of mineral trioxide aggregate. Int Endod J. 41:108–116. 2008.

85 

Shie MY, Huang TH, Kao CT, Huang CH and Ding SJ: The effect of a physiologic solution pH on properties of white mineral trioxide aggregate. J Endod. 35:98–101. 2009. View Article : Google Scholar

86 

Widbiller M, Lindner SR, Buchalla W, Eidt A, Hiller KA, Schmalz G and Galler KM: Three-dimensional culture of dental pulp stem cells in direct contact to tricalcium silicate cements. Clin Oral Investig. 20:237–246. 2016. View Article : Google Scholar

87 

Chen S, Gluhak-Heinrich J, Wang YH, Wu YM, Chuang HH, Chen L, Yuan GH, Dong J, Gay I and MacDougall M: Runx2, osx, and dspp in tooth development. J Dent Res. 88:904–909. 2009. View Article : Google Scholar : PubMed/NCBI

88 

Li S, Kong H, Yao N, Yu Q, Wang P, Lin Y, Wang J, Kuang R, Zhao X, Xu J, et al: The role of runt-related transcription factor 2 (Runx2) in the late stage of odontoblast differentiation and dentin formation. Biochem Biophys Res Commun. 410:698–704. 2011. View Article : Google Scholar : PubMed/NCBI

89 

Lambrichts I, Driesen RB, Dillen Y, Gervois P, Ratajczak J, Vangansewinkel T, Wolfs E, Bronckaers A and Hilkens P: Dental pulp stem cells: Their potential in reinnervation and angiogenesis by using Scaffolds. J Endod. 43:S12–S16. 2017. View Article : Google Scholar : PubMed/NCBI

90 

Brown LF, Detmar M, Claffey K, Nagy JA, Feng D, Dvorak AM and Dvorak HF: Vascular permeability factor/vascular endothelial growth factor: A multifunctional angiogenic cytokine. EXS. 79:233–269. 1997.PubMed/NCBI

91 

Folkman J and Shing Y: Angiogenesis. J Biol Chem. 267:10931–10934. 1992. View Article : Google Scholar : PubMed/NCBI

92 

Bai F, Wang Z, Lu J, Liu J, Chen G, Lv R, Wang J, Lin K, Zhang J and Huang X: The correlation between the internal structure and vascularization of controllable porous bioceramic materials in vivo: A quantitative study. Tissue Eng Part A. 16:3791–3803. 2010. View Article : Google Scholar : PubMed/NCBI

93 

Wang J, Fangteng JZ and Liu H: Effect of iRoot BP Plus on biological behavior of deciduous tooth pulp stem cells and human pulp stem cells. Shanghai Kou Qiang Yi Xue. 28:251–258. 2019.In Chinese. PubMed/NCBI

94 

Zhu L, Yang J, Zhang J, Lei D, Xiao L, Cheng X, Lin Y and Peng B: In vitro and in vivo evaluation of a nanoparticulate bioceramic paste for dental pulp repair. Acta Biomater. 10:5156–5168. 2014. View Article : Google Scholar : PubMed/NCBI

95 

Kuo JC: Mechanotransduction at focal adhesions: Integrating cytoskeletal mechanics in migrating cells. J Cell Mol Med. 17:704–712. 2013. View Article : Google Scholar : PubMed/NCBI

96 

Plotnikov SV and Waterman CM: Guiding cell migration by tugging. Curr Opin Cell Biol. 25:619–626. 2013. View Article : Google Scholar : PubMed/NCBI

97 

Sun Y, Luo T, Shen Y, Haapasalo M, Zou L and Liu J: Effect of iRoot fast set root repair material on the proliferation, migration and differentiation of human dental pulp stem cells in vitro. PLoS One. 12:e01868482017. View Article : Google Scholar : PubMed/NCBI

98 

Sun Y, Liu J, Luo T, Shen Y and Zou L: Effects of two fast-setting pulp-capping materials on cell viability and osteogenic differentiation in human dental pulp stem cells: An in vitro study. Arch Oral Biol. 100:100–105. 2019. View Article : Google Scholar : PubMed/NCBI

99 

Collado-Gonzalez M, Lopez-Garcia S, Garcia-Bernal D, Onate-Sanchez RE, Tomas-Catala CJ, Moraleda JM, Lozano A, Forner L and Rodriguez-Lozano FJ: Biological effects of acid-eroded MTA Repair HP and ProRoot MTA on human periodontal ligament stem cells. Clin Oral Investig. 23:3915–3924. 2019. View Article : Google Scholar : PubMed/NCBI

100 

Collado-Gonzalez M, Garcia-Bernal D, Onate-Sanchez RE, Ortolani-Seltenerich PS, Lozano A, Forner L, Llena C and Rodriguez-Lozano FJ: Biocompatibility of three new calcium silicate-based endodontic sealers on human periodontal ligament stem cells. Int Endod J. 50:875–884. 2017. View Article : Google Scholar

101 

Collado-Gonzalez M, Tomas-Catala CJ, Onate-Sanchez RE, Moraleda JM and Rodriguez-Lozano FJ: Cytotoxicity of GuttaFlow Bioseal, GuttaFlow2, MTA Fillapex, and AH Plus on human periodontal ligament stem cells. J Endod. 43:816–822. 2017. View Article : Google Scholar : PubMed/NCBI

102 

Rodriguez-Lozano FJ, Garcia-Bernal D, Onate-Sanchez RE, Ortolani-Seltenerich PS, Forner L and Moraleda JM: Evaluation of cytocompatibility of calcium silicate-based endodontic sealers and their effects on the biological responses of mesenchymal dental stem cells. Int Endod J. 50:67–76. 2017. View Article : Google Scholar

103 

Wang Y, Zhou Y, Jin L, Pang X, Lu Y, Wang Z, Yu Y and Yu J: Mineral trioxide aggregate enhances the osteogenic capacity of periodontal ligament stem cells via NF-κB and MAPK signaling pathways. J Cell Physiol. 233:2386–2397. 2018. View Article : Google Scholar

104 

Abuarqoub D, Aslam N, Jafar H, Abu Harfil Z and Awidi A: Biocompatibility of Biodentine™(R) with periodontal ligament stem cells: In vitro study. Dent J (Basel). 8:172020. View Article : Google Scholar

105 

Hakki SS, Bozkurt SB, Ozcopur B, Purali N and Belli S: Periodontal ligament fibroblast response to root perforations restored with different materials: A laboratory study. Int Endod J. 45:240–248. 2012. View Article : Google Scholar

106 

Lee MN, Hwang HS, Oh SH, Roshanzadeh A, Kim JW, Song JH, Kim ES and Koh JT: Elevated extracellular calcium ions promote proliferation and migration of mesenchymal stem cells via increasing osteopontin expression. Exp Mol Med. 50:1–16. 2018. View Article : Google Scholar : PubMed/NCBI

107 

D'Anto V, Di Caprio MP, Ametrano G, Simeone M, Rengo S and Spagnuolo G: Effect of mineral trioxide aggregate on mesenchymal stem cells. J Endod. 36:1839–1843. 2010. View Article : Google Scholar : PubMed/NCBI

108 

Eid AA, Hussein KA, Niu LN, Li GH, Watanabe I, Al-Shabrawey M, Pashley DH and Tay FR: Effects of tricalcium silicate cements on osteogenic differentiation of human bone marrow-derived mesenchymal stem cells in vitro. Acta Biomater. 10:3327–3334. 2014. View Article : Google Scholar : PubMed/NCBI

109 

Edrees HY, Abu Zeid ST, Atta HM and AlQriqri MA: Induction of osteogenic differentiation of mesenchymal stem cells by bioceramic root repair material. Materials (Basel). 12:23112019. View Article : Google Scholar

110 

Wang Y, Li J, Song W and Yu J: Mineral trioxide aggregate upregulates odonto/osteogenic capacity of bone marrow stromal cells from craniofacial bones via JNK and ERK MAPK signalling pathways. Cell Prolif. 47:241–248. 2014. View Article : Google Scholar : PubMed/NCBI

111 

Vidovic Zdrilic I, de Azevedo Queiroz IO, Matthews BG, Gomes-Filho JE, Mina M and Kalajzic I: Mineral trioxide aggregate improves healing response of periodontal tissue to injury in mice. J Periodontal Res. 52:1058–1067. 2017. View Article : Google Scholar : PubMed/NCBI

112 

Moon HJ, Lee JH, Kim JH, Knowles JC, Cho YB, Shin DH, Lee HH and Kim HW: Reformulated mineral trioxide aggregate components and the assessments for use as future dental regenerative cements. J Tissue Eng. 9:20417314188073962018. View Article : Google Scholar : PubMed/NCBI

113 

Gandolfi MG, Ciapetti G, Perut F, Taddei P, Modena E, Rossi PL and Prati C: Biomimetic calcium-silicate cements aged in simulated body solutions. Osteoblast response and analyses of apatite coating. J Appl Biomater Biomech. 7:160–170. 2009.

114 

Lu J, Li Z, Wu X, Chen Y, Yan M, Ge X and Yu J: iRoot BP Plus promotes osteo/odontogenic differentiation of bone marrow mesenchymal stem cells via MAPK pathways and autophagy. Stem Cell Res Ther. 10:2222019. View Article : Google Scholar : PubMed/NCBI

115 

De-Deus G, Canabarro A, Alves G, Linhares A, Senne MI and Granjeiro JM: Optimal cytocompatibility of a bioceramic nanoparticulate cement in primary human mesenchymal cells. J Endod. 35:1387–1390. 2009. View Article : Google Scholar : PubMed/NCBI

116 

Fathy SM, Abd El-Aziz AM and Labah DA: Cellular interaction and antibacterial efficacy of two hydraulic calcium silicate-based cements: Cell-dependent model. J Conserv Dent. 22:17–22. 2019.PubMed/NCBI

117 

Margunato S, Tasli PN, Aydin S, Karapınar Kazandağ M and Sahin F: In Vitro evaluation of ProRoot MTA, biodentine, and MM-MTA on human alveolar bone marrow stem cells in terms of biocompatibility and mineralization. J Endod. 41:1646–1652. 2015. View Article : Google Scholar : PubMed/NCBI

118 

Sultana N, Singh M, Nawal RR, Chaudhry S, Yadav S, Mohanty S and Talwar S: Evaluation of biocompatibility and osteogenic potential of tricalcium silicate-based cements using human bone marrow-derived mesenchymal stem cells. J Endod. 44:446–451. 2018. View Article : Google Scholar : PubMed/NCBI

119 

Costa F, Sousa Gomes P and Fernandes MH: Osteogenic and angiogenic response to calcium silicate-based endodontic sealers. J Endod. 42:113–119. 2016. View Article : Google Scholar

120 

Ali MRW, Mustafa M, Bardsen A and Bletsa A: Tricalcium silicate cements: Osteogenic and angiogenic responses of human bone marrow stem cells. Eur J Oral Sci. 127:261–268. 2019. View Article : Google Scholar : PubMed/NCBI

121 

Grech L, Mallia B and Camilleri J: Characterization of set Intermediate Restorative Material, Biodentine, Bioaggregate and a prototype calcium silicate cement for use as root-end filling materials. Int Endod J. 46:632–641. 2013. View Article : Google Scholar : PubMed/NCBI

122 

Kang JY, Lee BN, Son HJ, Koh JT, Kang SS, Son HH, Chang HS, Hwang IN, Hwang YC and Oh WM: Biocompatibility of mineral trioxide aggregate mixed with hydration accelerators. J Endod. 39:497–500. 2013. View Article : Google Scholar : PubMed/NCBI

123 

Silva EJ, Rosa TP, Herrera DR, Jacinto RC, Gomes BP and Zaia AA: Evaluation of cytotoxicity and physicochemical properties of calcium silicate-based endodontic sealer MTA Fillapex. J Endod. 39:274–277. 2013. View Article : Google Scholar : PubMed/NCBI

124 

Estrela C, Alencar AH, Kitten GT, Vencio EF and Gava E: Mesenchymal stem cells in the dental tissues: Perspectives for tissue regeneration. Braz Dent J. 22:91–98. 2011. View Article : Google Scholar : PubMed/NCBI

125 

Collado-Gonzalez M, Garcia-Bernal D, Onate-Sanchez RE, Ortolani-Seltenerich PS, Alvarez-Muro T, Lozano A, Forner L, Llena C, Moraleda JM and Rodriguez-Lozano FJ: Cytotoxicity and bioactivity of various pulpotomy materials on stem cells from human exfoliated primary teeth. Int Endod J. 50(Suppl 2): e19–e30. 2017. View Article : Google Scholar : PubMed/NCBI

126 

Araujo LB, Cosme-Silva L, Fernandes AP, Oliveira TM, Cavalcanti BDN, Gomes Filho JE and Sakai VT: Effects of mineral trioxide aggregate, BiodentineTM and calcium hydroxide on viability, proliferation, migration and differentiation of stem cells from human exfoliated deciduous teeth. J Appl Oral Sci. 26:e201606292018. View Article : Google Scholar : PubMed/NCBI

127 

Dahake PT, Panpaliya NP, Kale YJ, Dadpe MV, Kendre SB and Bogar C: Response of stem cells from human exfoliated deciduous teeth (SHED) to three bioinductive materials-An in vitro experimental study. Saudi Dent J. 32:43–51. 2020. View Article : Google Scholar : PubMed/NCBI

128 

Hasweh N, Awidi A, Rajab L, Hiyasat A, Jafar H, Islam N, Hasan M and Abuarqoub D: Characterization of the biological effect of Biodentine(TM) on primary dental pulp stem cells. Indian J Dent Res. 29:787–793. 2018. View Article : Google Scholar : PubMed/NCBI

129 

Athanasiadou E, Paschalidou M, Theocharidou A, Kontoudakis N, Arapostathis K and Bakopoulou A: Biological interactions of a calcium silicate based cement (Biodentine) with stem cells from human exfoliated deciduous teeth. Dent Mater. 34:1797–1813. 2018. View Article : Google Scholar : PubMed/NCBI

130 

Tsai CL, Ke MC, Chen YH, Kuo HK, Yu HJ, Chen CT, Tseng YC, Chuang PC and Wu PC: Mineral trioxide aggregate affects cell viability and induces apoptosis of stem cells from human exfoliated deciduous teeth. BMC Pharmacol Toxicol. 19:212018. View Article : Google Scholar : PubMed/NCBI

131 

Saidon J, He J, Zhu Q, Safavi K and Spangberg LS: Cell and tissue reactions to mineral trioxide aggregate and Portland cement. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 95:483–489. 2003. View Article : Google Scholar : PubMed/NCBI

132 

Torabinejad M, Hong CU, McDonald F and Pitt Ford TR: Physical and chemical properties of a new root-end filling material. J Endod. 21:349–353. 1995. View Article : Google Scholar : PubMed/NCBI

133 

Wongwatanasanti N, Jantarat J, Sritanaudomchai H and Hargreaves KM: Effect of bioceramic materials on proliferation and odontoblast differentiation of human stem cells from the apical papilla. J Endod. 44:1270–1275. 2018. View Article : Google Scholar : PubMed/NCBI

134 

Peters OA, Galicia J, Arias A, Tolar M, Ng E and Shin SJ: Effects of two calcium silicate cements on cell viability, angiogenic growth factor release and related gene expression in stem cells from the apical papilla. Int Endod J. 49:1132–1140. 2016. View Article : Google Scholar

135 

Schneider R, Holland GR, Chiego D Jr, Hu JC, Nör JE and Botero TM: White mineral trioxide aggregate induces migration and proliferation of stem cells from the apical papilla. J Endod. 40:931–936. 2014. View Article : Google Scholar : PubMed/NCBI

136 

Saberi EA, Karkehabadi H and Mollashahi NF: Cytotoxicity of various endodontic materials on stem cells of human apical papilla. Iran Endod J. 11:17–22. 2016.PubMed/NCBI

137 

Miller AA, Takimoto K, Wealleans J and Diogenes A: Effect of 3 bioceramic materials on stem cells of the apical papilla proliferation and differentiation using a dentin disk model. J Endod. 44:599–603. 2018. View Article : Google Scholar : PubMed/NCBI

138 

Du J, Lu Y, Song M, Yang L, Liu J, Chen X, Ma Y and Wang Y: Effects of ERK/p38 MAPKs signaling pathways on MTA-mediated osteo/odontogenic differentiation of stem cells from apical papilla: A vitro study. BMC Oral Health. 20:502020. View Article : Google Scholar : PubMed/NCBI

139 

Saberi E, Farhad-Mollashahi N, Sargolzaei Aval F and Saberi M: Proliferation, odontogenic/osteogenic differentiation, and cytokine production by human stem cells of the apical papilla induced by biomaterials: A comparative study. Clin Cosmet Investig Dent. 11:181–193. 2019. View Article : Google Scholar : PubMed/NCBI

140 

Hajizadeh N, Madani ZS, Zabihi E, Golpour M, Zahedpasha A and Mohammadnia M: Effect of MTA and CEM on mineralization-associated gene expression in stem cells derived from apical papilla. Iran Endod J. 13:94–101. 2018.PubMed/NCBI

141 

Chang J, Liu F, Lee M, Wu B, Ting K, Zara JN, Soo C, Al Hezaimi K, Zou W, Chen X, et al: NF-κB inhibits osteogenic differentiation of mesenchymal stem cells by promoting β-catenin degradation. Proc Natl Acad Sci USA. 110:9469–9474. 2013. View Article : Google Scholar

142 

Yan M, Wu J, Yu Y, Wang Y, Xie L, Zhang G, Yu J and Zhang C: Mineral trioxide aggregate promotes the odonto/osteogenic differentiation and dentinogenesis of stem cells from apical papilla via nuclear factor kappa B signaling pathway. J Endod. 40:640–647. 2014. View Article : Google Scholar : PubMed/NCBI

143 

Li H and Chang J: Bioactive silicate materials stimulate angiogenesis in fibroblast and endothelial cell co-culture system through paracrine effect. Acta Biomater. 9:6981–6991. 2013. View Article : Google Scholar : PubMed/NCBI

144 

Day RM: Bioactive glass stimulates the secretion of angiogenic growth factors and angiogenesis in vitro. Tissue Eng. 11:768–777. 2005. View Article : Google Scholar : PubMed/NCBI

145 

Leu A and Leach JK: Proangiogenic potential of a collagen/bioactive glass substrate. Pharm Res. 25:1222–1229. 2008. View Article : Google Scholar

146 

Wang G, Roohani-Esfahani SI, Zhang W, Lv K, Yang G, Ding X, Zou D, Cui D, Zreiqat H and Jiang X: Effects of Sr-HT-Gahnite on osteogenesis and angiogenesis by adipose derived stem cells for critical-sized calvarial defect repair. Sci Rep. 7:411352017. View Article : Google Scholar : PubMed/NCBI

147 

Liu Y, Liu XM, Bi J, Yu S, Yang N, Song B and Chen X: Cell migration and osteo/odontogenesis stimulation of iRoot FS as a potential apical barrier material in apexification. Int Endod J. 53:467–477. 2020. View Article : Google Scholar

148 

Bi J, Liu Y, Liu XM, Jiang LM and Chen X: iRoot FM exerts an antibacterial effect on Porphyromonas endodontalis and improves the properties of stem cells from the apical papilla. Int Endod J. 51:1139–1148. 2018. View Article : Google Scholar : PubMed/NCBI

149 

Dogan A, Yalvac ME, Sahin F, Kabanov AV, Palotas A and Rizvanov AA: Differentiation of human stem cells is promoted by amphiphilic pluronic block copolymers. Int J Nanomedicine. 7:4849–4860. 2012.PubMed/NCBI

150 

Dogan A, Demirci S and Sahin F: In vitro differentiation of human tooth germ stem cells into endothelial- and epithelial-like cells. Cell Biol Int. 39:94–103. 2015. View Article : Google Scholar

151 

Guven EP, Yalvac ME, Sahin F, Yazici MM, Rizvanov AA and Bayirli G: Effect of dental materials calcium hydroxidecontaining cement, mineral trioxide aggregate, and enamel matrix derivative on proliferation and differentiation of human tooth germ stem cells. J Endod. 37:650–656. 2011. View Article : Google Scholar : PubMed/NCBI

152 

Guven EP, Yalvac ME, Kayahan MB, Sunay H, Sahin F and Bayirli G: Human tooth germ stem cell response to calcium-silicate based endodontic cements. J Appl Oral Sci. 21:351–357. 2013. View Article : Google Scholar : PubMed/NCBI

153 

Güven EP, Taşlı PN, Yalvac ME, Sofiev N, Kayahan MB and Sahin F: In vitro comparison of induction capacity and biomineralization ability of mineral trioxide aggregate and a bioceramic root canal sealer. Int Endod J. 46:1173–1182. 2013. View Article : Google Scholar : PubMed/NCBI

154 

Jiang N, Guo W, Chen M, Zheng Y, Zhou J, Kim SG, Embree MC, Songhee Song K, Marao HF and Mao JJ: Periodontal ligament and alveolar bone in health and adaptation: Tooth movement. Front Oral Biol. 18:1–8. 2016.

155 

Zhou Y, Wu C and Xiao Y: Silicate-based bioceramics for periodontal regeneration. J Mater Chem B. 2:3907–3910. 2014. View Article : Google Scholar : PubMed/NCBI

156 

Proksch S, Brossart J, Vach K, Hellwig E, Altenburger MJ and Karygianni L: Evaluation of the bioactivity of fluoride-enriched mineral trioxide aggregate on osteoblasts. Int Endod J. 51:912–923. 2018. View Article : Google Scholar : PubMed/NCBI

157 

Nakayama A, Ogiso B, Tanabe N, Takeichi O, Matsuzaka K and Inoue T: Behaviour of bone marrow osteoblast-like cells on mineral trioxide aggregate: Morphology and expression of type I collagen and bone-related protein mRNAs. Int Endod J. 38:203–210. 2005. View Article : Google Scholar : PubMed/NCBI

158 

Castro-Raucci LM, Teixeira LN, Oliveira IR, Raucci-Neto W, Jacobovitz M, Rosa AL and de Oliveira PT: Osteogenic cell response to calcium aluminate-based cement. Int Endod J. 50:771–779. 2017. View Article : Google Scholar

159 

Castro-Raucci LM, Oliveira IR, Teixeira LN, Rosa AL, Oliveira PT and Jacobovitz M: Effects of a novel calcium aluminate cement on the early events of the progression of osteogenic cell cultures. Braz Dent J. 22:99–104. 2011. View Article : Google Scholar : PubMed/NCBI

160 

Orrenius S, Zhivotovsky B and Nicotera P: Regulation of cell death: The calcium-apoptosis link. Nat Rev Mol Cell Biol. 4:552–565. 2003. View Article : Google Scholar : PubMed/NCBI

161 

Dvorak MM and Riccardi D: Ca2+ as an extracellular signal in bone. Cell Calcium. 35:249–255. 2004. View Article : Google Scholar : PubMed/NCBI

162 

Oliveira IR, Andrade TL, Jacobovitz M and Pandolfelli VC: Bioactivity of calcium aluminate endodontic cement. J Endod. 39:774–778. 2013. View Article : Google Scholar : PubMed/NCBI

163 

Pires-de-Souza FC, Moraes PC, Garcia Lda F, Aguilar FG and Watanabe E: Evaluation of pH, calcium ion release and antimicrobial activity of a new calcium aluminate cement. Braz Oral Res. 27:324–330. 2013. View Article : Google Scholar

164 

Scelza MZ, Nascimento JC, Silva LE, Gameiro VS, DE Deus G and Alves G: Biodentine™ is cytocompatible with human primary osteoblasts. Braz Oral Res. 31:e812017. View Article : Google Scholar

165 

Coelho MJ and Fernandes MH: Human bone cell cultures in biocompatibility testing. Part II: Effect of ascorbic acid, beta-glycerophosphate and dexamethasone on osteoblastic differentiation. Biomaterials. 21:1095–1102. 2000. View Article : Google Scholar : PubMed/NCBI

166 

Rifaey HS, Villa M, Zhu Q, Wang YH, Safavi K and Chen IP: Comparison of the osteogenic potential of mineral trioxide aggregate and endosequence root repair material in a 3-dimensional culture system. J Endod. 42:760–765. 2016. View Article : Google Scholar : PubMed/NCBI

167 

Ciasca M, Aminoshariae A, Jin G, Montagnese T and Mickel A: A comparison of the cytotoxicity and proinflammatory cytokine production of EndoSequence root repair material and ProRoot mineral trioxide aggregate in human osteoblast cell culture using reverse-transcriptase polymerase chain reaction. J Endod. 38:486–489. 2012. View Article : Google Scholar : PubMed/NCBI

168 

Tani-Ishii N, Hamada N, Watanabe K, Tujimoto Y, Teranaka T and Umemoto T: Expression of bone extracellular matrix proteins on osteoblast cells in the presence of mineral trioxide. J Endod. 33:836–839. 2007. View Article : Google Scholar : PubMed/NCBI

169 

Yoshimine Y, Ono M and Akamine A: In vitro comparison of the biocompatibility of mineral trioxide aggregate, 4META/MMA-TBB resin, and intermediate restorative material as root-end-filling materials. J Endod. 33:1066–1069. 2007. View Article : Google Scholar : PubMed/NCBI

170 

Maeda T, Suzuki A, Yuzawa S, Baba Y, Kimura Y and Kato Y: Mineral trioxide aggregate induces osteoblastogenesis via Atf6. Bone Rep. 2:36–43. 2015. View Article : Google Scholar : PubMed/NCBI

171 

Lee GW, Yoon JH, Jang JH, Chang HS, Hwang YC, Hwang IN, Oh WM and Lee BN: Effects of newly-developed retrograde filling material on osteoblastic differentiation in vitro. Dent Mater J. 38:528–533. 2019. View Article : Google Scholar : PubMed/NCBI

172 

Sarkar NK, Caicedo R, Ritwik P, Moiseyeva R and Kawashima I: Physicochemical basis of the biologic properties of mineral trioxide aggregate. J Endod. 31:97–100. 2005. View Article : Google Scholar : PubMed/NCBI

173 

Estrela C, Sydney GB, Pesce HF and Felippe Júnior O: Dentinal diffusion of hydroxyl ions of various calcium hydroxide pastes. Braz Dent J. 6:5–9. 1995.PubMed/NCBI

174 

Ko H, Yang W, Park K and Kim M: Cytotoxicity of mineral trioxide aggregate (MTA) and bone morphogenetic protein 2 (BMP-2) and response of rat pulp to MTA and BMP-2. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 109:e103–e108. 2010. View Article : Google Scholar : PubMed/NCBI

175 

Wozney JM: The bone morphogenetic protein family: Multifunctional cellular regulators in the embryo and adult. Eur J Oral Sci. 106(Suppl 1): S160–S166. 1998. View Article : Google Scholar

176 

Zhu Q, Haglund R, Safavi KE and Spangberg LS: Adhesion of human osteoblasts on root-end filling materials. J Endod. 26:404–406. 2000. View Article : Google Scholar

177 

Pelliccioni GA, Ciapetti G, Cenni E, Granchi D, Nanni M, Pagani S and Giunti A: Evaluation of osteoblast-like cell response to Proroot MTA (mineral trioxide aggregate) cement. J Mater Sci Mater Med. 15:167–173. 2004. View Article : Google Scholar : PubMed/NCBI

178 

Tanomaru-Filho M, Andrade AS, Rodrigues EM, Viola KS, Faria G, Camilleri J and Guerreiro-Tanomaru JM: Biocompatibility and mineralized nodule formation of Neo MTA Plus and an experimental tricalcium silicate cement containing tantalum oxide. Int Endod J. 50(Suppl 2): e31–e39. 2017. View Article : Google Scholar : PubMed/NCBI

179 

Modareszadeh MR, Di Fiore PM, Tipton DA and Salamat N: Cytotoxicity and alkaline phosphatase activity evaluation of endosequence root repair material. J Endod. 38:1101–1105. 2012. View Article : Google Scholar : PubMed/NCBI

180 

Yuan Z, Peng B, Jiang H, Bian Z and Yan P: Effect of bioaggregate on mineral-associated gene expression in osteoblast cells. J Endod. 36:1145–1148. 2010. View Article : Google Scholar : PubMed/NCBI

181 

Jung S, Mielert J, Kleinheinz J and Dammaschke T: Human oral cells' response to different endodontic restorative materials: An in vitro study. Head Face Med. 10:552014. View Article : Google Scholar : PubMed/NCBI

182 

Attik GN, Villat C, Hallay F, Pradelle-Plasse N, Bonnet H, Moreau K, Colon P and Grosgogeat B: In vitro biocompatibility of a dentine substitute cement on human MG63 osteoblasts cells: Biodentine versus MTA((®)). Int Endod J. 47:1133–1141. 2014. View Article : Google Scholar : PubMed/NCBI

183 

Kim HS, Kim S, Ko H, Song M and Kim M: Effects of the cathepsin K inhibitor with mineral trioxide aggregate cements on osteoclastic activity. Restor Dent Endod. 44:e172019. View Article : Google Scholar : PubMed/NCBI

184 

Gomes-Cornelio AL, Rodrigues EM, Salles LP, Mestieri LB, Faria G, Guerreiro-Tanomaru JM and Tanomaru-Filho M: Bioactivity of MTA Plus, Biodentine and an experimental calcium silicate-based cement on human osteoblast-like cells. Int Endod J. 50:39–47. 2017. View Article : Google Scholar

185 

De-Deus G, Canabarro A, Alves GG, Marins JR, Linhares AB and Granjeiro JM: Cytocompatibility of the ready-to-use bioceramic putty repair cement iRoot BP Plus with primary human osteoblasts. Int Endod J. 45:508–513. 2012. View Article : Google Scholar : PubMed/NCBI

186 

Tian J, Zhang Y, Lai Z, Li M, Huang Y, Jiang H and Wei X: Ion release, microstructural, and biological properties of iRoot BP Plus and ProRoot MTA exposed to an acidic environment. J Endod. 43:163–168. 2017. View Article : Google Scholar

187 

Lv F, Zhu L, Zhang J, Yu J, Cheng X and Peng B: Evaluation of the in vitro biocompatibility of a new fast-setting ready-to-use root filling and repair material. Int Endod J. 50:540–548. 2017. View Article : Google Scholar

188 

Jiang Y, Zheng Q, Zhou X, Gao Y and Huang D: A comparative study on root canal repair materials: A cytocompatibility assessment in L929 and MG63 cells. ScientificWorldJournal. 2014:4638262014. View Article : Google Scholar : PubMed/NCBI

189 

Levine BR, Sporer S, Poggie RA, Della Valle CJ and Jacobs JJ: Experimental and clinical performance of porous tantalum in orthopedic surgery. Biomaterials. 27:4671–4681. 2006. View Article : Google Scholar : PubMed/NCBI

190 

Zhang W, Li Z and Peng B: Effects of iRoot SP on mineralization-related genes expression in MG63 cells. J Endod. 36:1978–1982. 2010. View Article : Google Scholar : PubMed/NCBI

191 

Zhang J, Zhu L and Peng B: Effect of BioAggregate on osteoclast differentiation and inflammatory bone resorption in vivo. Int Endod J. 48:1077–1085. 2015. View Article : Google Scholar

192 

Tian J, Qi W, Zhang Y, Glogauer M, Wang Y, Lai Z and Jiang H: Bioaggregate inhibits osteoclast differentiation, fusion, and bone resorption in vitro. J Endodont. 41:1500–1506. 2015. View Article : Google Scholar

193 

Zhang J, Zhu L, Yan P and Peng B: Effect of BioAggregate on receptor activator of nuclear factor-kappa B ligand-induced osteoclastogenesis from murine macrophage cell line in vitro. J Endod. 41:1265–1271. 2015. View Article : Google Scholar : PubMed/NCBI

194 

Cheng X, Zhu L, Zhang J, Yu J, Liu S, Lv F, Lin Y, Liu G and Peng B: Anti-osteoclastogenesis of mineral trioxide aggregate through inhibition of the autophagic pathway. J Endodont. 43:766–773. 2017. View Article : Google Scholar

195 

Hashiguchi D, Fukushima H, Nakamura M, Morikawa K, Yasuda H, Udagawa N, Maki K and Jimi E: Mineral trioxide aggregate solution inhibits osteoclast differentiation through the maintenance of osteoprotegerin expression in osteoblasts. J Biomed Mater Res A. 96:358–364. 2011. View Article : Google Scholar

196 

Hashiguchi D, Fukushima H, Yasuda H, Masuda W, Tomikawa M, Morikawa K, Maki K and Jimi E: Mineral trioxide aggregate inhibits osteoclastic bone resorption. J Dent Res. 90:912–917. 2011. View Article : Google Scholar : PubMed/NCBI

197 

Kim M, Kim S, Ko H and Song M: Effect of ProRoot MTA® and Biodentine® on osteoclastic differentiation and activity of mouse bone marrow macrophages. J Appl Oral Sci. 27:e201801502019. View Article : Google Scholar

198 

Choi SC, Kwon YD, Kim KC and Kim GT: The effects of topical application of bisphosphonates on replanted rat molars. Dent Traumatol. 26:476–480. 2010. View Article : Google Scholar : PubMed/NCBI

199 

Komatsu K, Shimada A, Shibata T, Shimoda S, Oida S, Kawasaki K and Nifuji A: Long-term effects of local pretreatment with alendronate on healing of replanted rat teeth. J Periodontal Res. 43:194–200. 2008. View Article : Google Scholar : PubMed/NCBI

200 

Tu MG, Sun KT, Wang TH, He YZ, Hsia SM, Tsai BH, Shih YH and Shieh TM: Effects of mineral trioxide aggregate and bioceramics on macrophage differentiation and polarization in vitro. J Formos Med Assoc. 118:1458–1465. 2019. View Article : Google Scholar : PubMed/NCBI

201 

Camilleri J: Characterization of hydration products of mineral trioxide aggregate. Int Endod J. 41:408–417. 2008. View Article : Google Scholar : PubMed/NCBI

202 

Varanasi VG, Leong KK, Dominia LM, Jue SM, Loomer PM and Marshall GW: Si and Ca individually and combinatorially target enhanced MC3T3-E1 subclone 4 early osteogenic marker expression. J Oral Implantol. 38:325–336. 2012. View Article : Google Scholar : PubMed/NCBI

203 

Xia L, Yin Z, Mao L, Wang X, Liu J, Jiang X, Zhang Z, Lin K, Chang J and Fang B: Akermanite bioceramics promote osteogenesis, angiogenesis and suppress osteoclastogenesis for osteoporotic bone regeneration. Sci Rep. 6:220052016. View Article : Google Scholar : PubMed/NCBI

204 

Wu C, Chen Z, Yi D, Chang J and Xiao Y: Multidirectional effects of Sr-, Mg-, and Si-containing bioceramic coatings with high bonding strength on inflammation, osteoclastogenesis, and osteogenesis. ACS Appl Mater Interfaces. 6:4264–4276. 2014. View Article : Google Scholar : PubMed/NCBI

205 

Hung CJ, Kao CT, Chen YJ, Shie MY and Huang TH: Antiosteoclastogenic activity of silicate-based materials antagonizing receptor activator for nuclear factor kappaB ligand-induced osteoclast differentiation of murine marcophages. J Endod. 39:1557–1561. 2013. View Article : Google Scholar : PubMed/NCBI

206 

Sun T, Wang M, Shao Y, Wang L and Zhu Y: The effect and osteoblast signaling response of trace silicon doping hydroxyapatite. Biol Trace Elem Res. 181:82–94. 2018. View Article : Google Scholar

207 

Wang S, Wang X, Draenert FG, Albert O, Schroder HC, Mailander V, Mitov G and Muller WE: Bioactive and biodegradable silica biomaterial for bone regeneration. Bone. 67:292–304. 2014. View Article : Google Scholar : PubMed/NCBI

208 

Zhai W, Lu H, Wu C, Chen L, Lin X, Naoki K, Chen G and Chang J: Stimulatory effects of the ionic products from Ca-Mg-Si bioceramics on both osteogenesis and angiogenesis in vitro. Acta Biomater. 9:8004–8014. 2013. View Article : Google Scholar : PubMed/NCBI

209 

Gough JE, Notingher I and Hench LL: Osteoblast attachment and mineralized nodule formation on rough and smooth 45S5 bioactive glass monoliths. J Biomed Mater Res A. 68:640–650. 2004. View Article : Google Scholar : PubMed/NCBI

210 

Gough JE, Clupper DC and Hench LL: Osteoblast responses to tape-cast and sintered bioactive glass ceramics. J Biomed Mater Res A. 69:621–628. 2004. View Article : Google Scholar : PubMed/NCBI

211 

Ibrahim S, Sabudin S, Sahid S, Marzuke MA, Hussin ZH, Kader Bashah NS and Jamuna-Thevi K: Bioactivity studies and adhesion of human osteoblast (hFOB) on silicon-biphasic calcium phosphate material. Saudi J Biol Sci. 23:S56–S63. 2016. View Article : Google Scholar : PubMed/NCBI

212 

Caudrillier A, Hurtel-Lemaire AS, Wattel A, Cournarie F, Godin C, Petit L, Petit JP, Terwilliger E, Kamel S, Brown EM, et al: Strontium ranelate decreases receptor activator of nuclear factor-κB ligand-induced osteoclastic differentiation in vitro: Involvement of the calcium-sensing receptor. Mol Pharmacol. 78:569–576. 2010. View Article : Google Scholar : PubMed/NCBI

213 

Mladenovic Z, Johansson A, Willman B, Shahabi K, Bjorn E and Ransjo M: Soluble silica inhibits osteoclast formation and bone resorption in vitro. Acta Biomater. 10:406–418. 2014. View Article : Google Scholar

214 

Okabe T, Sakamoto M, Takeuchi H and Matsushima K: Effects of pH on mineralization ability of human dental pulp cells. J Endod. 32:198–201. 2006. View Article : Google Scholar : PubMed/NCBI

215 

Stuart CH, Schwartz SA, Beeson TJ and Owatz CB: Enterococcus faecalis: Its role in root canal treatment failure and current concepts in retreatment. J Endod. 32:93–98. 2006. View Article : Google Scholar : PubMed/NCBI

216 

Gao J, Wang M, Shi C, Wang L, Wang D and Zhu Y: Synthesis of trace element Si and Sr codoping hydroxyapatite with non-cytotoxicity and enhanced cell proliferation and differentiation. Biol Trace Elem Res. 174:208–217. 2016. View Article : Google Scholar : PubMed/NCBI

217 

Lin LM and Rosenberg PA: Repair and regeneration in endodontics. Int Endod J. 44:889–906. 2011. View Article : Google Scholar : PubMed/NCBI

218 

Koulaouzidou EA, Economides N, Beltes P, Geromichalos G and Papazisis K: In vitro evaluation of the cytotoxicity of ProRoot MTA and MTA Angelus. J Oral Sci. 50:397–402. 2008. View Article : Google Scholar : PubMed/NCBI

219 

Peng W, Liu W, Zhai W, Jiang L, Li L, Chang J and Zhu Y: Effect of tricalcium silicate on the proliferation and odontogenic differentiation of human dental pulp cells. J Endod. 37:1240–1246. 2011. View Article : Google Scholar : PubMed/NCBI

220 

Kim DH, Jang JH, Lee BN, Chang HS, Hwang IN, Oh WM, Kim SH, Min KS, Koh JT and Hwang YC: Anti-inflammatory and mineralization effects of ProRoot MTA and endocem MTA in studies of human and rat dental pulps in vitro and in vivo. J Endod. 44:1534–1541. 2018. View Article : Google Scholar : PubMed/NCBI

221 

Liu CH, Huang TH, Hung CJ, Lai WY, Kao CT and Shie MY: The synergistic effects of fibroblast growth factor-2 and mineral trioxide aggregate on an osteogenic accelerator in vitro. Int Endod J. 47:843–853. 2014. View Article : Google Scholar

222 

Chung CJ, Kim E, Song M, Park JW and Shin SJ: Effects of two fast-setting calcium-silicate cements on cell viability and angiogenic factor release in human pulp-derived cells. Odontology. 104:143–151. 2016. View Article : Google Scholar

223 

Chang SW, Lee SY, Kum KY and Kim EC: Effects of ProRoot MTA, Bioaggregate, and Micromega MTA on odontoblastic differentiation in human dental pulp cells. J Endod. 40:113–118. 2014. View Article : Google Scholar

224 

Jung JY, Woo SM, Lee BN, Koh JT, Nor JE and Hwang YC: Effect of Biodentine and Bioaggregate on odontoblastic differentiation via mitogen-activated protein kinase pathway in human dental pulp cells. Int Endod J. 48:177–184. 2015. View Article : Google Scholar

225 

Zhu L, Yang J, Zhang J and Peng B: A comparative study of BioAggregate and ProRoot MTA on adhesion, migration, and attachment of human dental pulp cells. J Endod. 40:1118–1123. 2014. View Article : Google Scholar : PubMed/NCBI

226 

Zhang S, Yang X and Fan M: BioAggregate and iRoot BP Plus optimize the proliferation and mineralization ability of human dental pulp cells. Int Endod J. 46:923–929. 2013. View Article : Google Scholar : PubMed/NCBI

227 

Tomson PL, Grover LM, Lumley PJ, Sloan AJ, Smith AJ and Cooper PR: Dissolution of bio-active dentine matrix components by mineral trioxide aggregate. J Dent. 35:636–642. 2007. View Article : Google Scholar : PubMed/NCBI

228 

Laurent P, Camps J and About I: Biodentine(TM) induces TGF-β1 release from human pulp cells and early dental pulp mineralization. Int Endod J. 45:439–448. 2012. View Article : Google Scholar

229 

Zanini M, Sautier JM, Berdal A and Simon S: Biodentine induces immortalized murine pulp cell differentiation into odontoblast-like cells and stimulates biomineralization. J Endod. 38:1220–1226. 2012. View Article : Google Scholar : PubMed/NCBI

230 

Liu S, Wang S and Dong Y: Evaluation of a bioceramic as a pulp capping agent in vitro and in vivo. J Endod. 41:652–657. 2015. View Article : Google Scholar : PubMed/NCBI

231 

Zhang J, Zhu LX, Cheng X, Lin Y, Yan P and Peng B: Promotion of dental pulp cell migration and pulp repair by a bioceramic putty involving FGFR-mediated signaling pathways. J Dent Res. 94:853–862. 2015. View Article : Google Scholar : PubMed/NCBI

232 

Kierat A, Laszczynska M, Kowalska E and Weyna E: Comparison of the influence of mineral trioxide aggregate and calcium hydroxide on dental pulp of permanent teeth in biological treatment and cell cultures. Ann Acad Med Stetin. 56:89–96. 2010.In Polish.

233 

Zakerzadeh A, Esnaashari E and Dadfar S: In Vitro comparison of cytotoxicity and genotoxicity of three vital pulp capping materials. Iran Endod J. 12:419–425. 2017.PubMed/NCBI

234 

Nikfarjam F, Beyer K, Konig A, Hofmann M, Butting M, Valesky E, Kippenberger S, Kaufmann R, Heidemann D, Bernd A and Zöller NN: Influence of Biodentine(R)-A dentine substitute-on collagen type i synthesis in pulp fibroblasts in vitro. PLoS One. 11:e1676332016. View Article : Google Scholar

235 

Begue-Kirn C, Smith AJ, Ruch JV, Wozney JM, Purchio A, Hartmann D and Lesot H: Effects of dentin proteins, transforming growth factor beta 1 (TGF beta 1) and bone morphogenetic protein 2 (BMP2) on the differentiation of odontoblast in vitro. Int J Dev Biol. 36:491–503. 1992.PubMed/NCBI

236 

Strong DD, Beachler AL, Wergedal JE and Linkhart TA: Insulinlike growth factor II and transforming growth factor beta regulate collagen expression in human osteoblastlike cells in vitro. J Bone Miner Res. 6:15–23. 1991. View Article : Google Scholar : PubMed/NCBI

237 

Helder MN, Bronckers AL and Woltgens JH: Dissimilar expression patterns for the extracellular matrix proteins osteopontin (OPN) and collagen type I in dental tissues and alveolar bone of the neonatal rat. Matrix. 13:415–425. 1993. View Article : Google Scholar : PubMed/NCBI

238 

Mathieu S, Jeanneau C, Sheibat-Othman N, Kalaji N, Fessi H and About I: Usefulness of controlled release of growth factors in investigating the early events of dentin-pulp regeneration. J Endod. 39:228–235. 2013. View Article : Google Scholar : PubMed/NCBI

239 

Shimabukuro Y, Ueda M, Ozasa M, Anzai J, Takedachi M, Yanagita M, Ito M, Hashikawa T, Yamada S and Murakami S: Fibroblast growth factor-2 regulates the cell function of human dental pulp cells. J Endod. 35:1529–1535. 2009. View Article : Google Scholar : PubMed/NCBI

240 

Giraud T, Jeanneau C, Bergmann M, Laurent P and About I: Tricalcium silicate capping materials modulate pulp healing and inflammatory activity in vitro. J Endod. 44:1686–1691. 2018. View Article : Google Scholar : PubMed/NCBI

241 

Guo RF and Ward PA: Role of C5a in inflammatory responses. Annu Rev Immunol. 23:821–852. 2005. View Article : Google Scholar : PubMed/NCBI

242 

Chmilewsky F, Jeanneau C, Dejou J and About I: Sources of dentin-pulp regeneration signals and their modulation by the local microenvironment. J Endod. 40(Suppl 4): S19–S25. 2014. View Article : Google Scholar : PubMed/NCBI

243 

Giraud T, Rufas P, Chmilewsky F, Rombouts C, Dejou J, Jeanneau C and About I: Complement activation by pulp capping materials plays a significant role in both inflammatory and pulp stem cells' recruitment. J Endod. 43:1104–1110. 2017. View Article : Google Scholar : PubMed/NCBI

244 

Karimjee CK, Koka S, Rallis DM and Gound TG: Cellular toxicity of mineral trioxide aggregate mixed with an alternative delivery vehicle. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 102:e115–e120. 2006. View Article : Google Scholar : PubMed/NCBI

245 

Maeda H, Nakano T, Tomokiyo A, Fujii S, Wada N, Monnouchi S, Hori K and Akamine A: Mineral trioxide aggregate induces bone morphogenetic protein-2 expression and calcification in human periodontal ligament cells. J Endod. 36:647–652. 2010. View Article : Google Scholar : PubMed/NCBI

246 

Kasaj A, Willershausen B, Reichert C, Rohrig B, Smeets R and Schmidt M: Ability of nanocrystalline hydroxyapatite paste to promote human periodontal ligament cell proliferation. J Oral Sci. 50:279–285. 2008. View Article : Google Scholar : PubMed/NCBI

247 

Wang MC, Yeh LY, Shih WY, Li WC, Chang KW and Lin SC: Portland cement induces human periodontal ligament cells to differentiate by upregulating miR-146a. J Formos Med Assoc. 117:308–315. 2018. View Article : Google Scholar

248 

Luo T, Liu J, Sun Y, Shen Y and Zou L: Cytocompatibility of Biodentine and iRoot FS with human periodontal ligament cells: An in vitro study. Int Endod J. 51:779–788. 2018. View Article : Google Scholar : PubMed/NCBI

249 

Chang SW, Lee SY, Kang SK, Kum KY and Kim EC: In vitro biocompatibility, inflammatory response, and osteogenic potential of 4 root canal sealers: Sealapex, Sankin apatite root sealer, MTA Fillapex, and iRoot SP root canal sealer. J Endod. 40:1642–1648. 2014. View Article : Google Scholar : PubMed/NCBI

250 

Willershausen I, Wolf T, Kasaj A, Weyer V, Willershausen B and Marroquin BB: Influence of a bioceramic root end material and mineral trioxide aggregates on fibroblasts and osteoblasts. Arch Oral Biol. 58:1232–1237. 2013. View Article : Google Scholar : PubMed/NCBI

251 

Gupta SK, Saxena P, Pant VA and Pant AB: Adhesion and biologic behavior of human periodontal fibroblast cells to resin ionomer Geristore: A comparative analysis. Dent Traumatol. 29:389–393. 2013. View Article : Google Scholar

252 

Balto HA: Attachment and morphological behavior of human periodontal ligament fibroblasts to mineral trioxide aggregate: A scanning electron microscope study. J Endod. 30:25–29. 2004. View Article : Google Scholar : PubMed/NCBI

253 

Bonson S, Jeansonne BG and Lallier TE: Root-end filling materials alter fibroblast differentiation. J Dent Res. 83:408–413. 2004. View Article : Google Scholar : PubMed/NCBI

254 

Gorduysus M, Avcu N, Gorduysus O, Pekel A, Baran Y, Avcu F and Ural AU: Cytotoxic effects of four different endodontic materials in human periodontal ligament fibroblasts. J Endod. 33:1450–1454. 2007. View Article : Google Scholar : PubMed/NCBI

255 

Badr AE: Marginal adaptation and cytotoxicity of bone cement compared with amalgam and mineral trioxide aggregate as root-end filling materials. J Endod. 36:1056–1060. 2010. View Article : Google Scholar : PubMed/NCBI

256 

Yoshino P, Nishiyama CK, Modena KC, Santos CF and Sipert CR: In vitro cytotoxicity of white MTA, MTA Fillapex(R) and Portland cement on human periodontal ligament fibroblasts. Braz Dent J. 24:111–116. 2013. View Article : Google Scholar

257 

Keiser K, Johnson CC and Tipton DA: Cytotoxicity of mineral trioxide aggregate using human periodontal ligament fibroblasts. J Endod. 26:288–291. 2000. View Article : Google Scholar

258 

Al-Haj Ali SN, Al-Jundi SH and Ditto DJ: In vitro toxicity of formocresol, ferric sulphate, and grey MTA on human periodontal ligament fibroblasts. Eur Arch Paediatr Dent. 16:51–55. 2015. View Article : Google Scholar

259 

Al-Haj AS: In vitro toxicity of propolis in comparison with other primary teeth pulpotomy agents on human fibroblasts. J Investig Clin Dent. 7:308–313. 2016. View Article : Google Scholar

260 

Samyuktha V, Ravikumar P, Nagesh B, Ranganathan K, Jayaprakash T and Sayesh V: Cytotoxicity evaluation of root repair materials in human-cultured periodontal ligament fibroblasts. J Conserv Dent. 17:467–470. 2014. View Article : Google Scholar : PubMed/NCBI

261 

Kucukkaya S, Gorduysus MO, Zeybek ND and Muftuoglu SF: In vitro cytotoxicity of calcium silicate-based endodontic cement as root-end filling materials. Scientifica (Cairo). 2016:92039322016.

262 

Jang YE, Lee BN, Koh JT, Park YJ, Joo NE, Chang HS, Hwang IN, Oh WM and Hwang YC: Cytotoxicity and physical properties of tricalcium silicate-based endodontic materials. Restor Dent Endod. 39:89–94. 2014. View Article : Google Scholar : PubMed/NCBI

263 

Akbulut MB, Arpaci PU and Eldeniz AU: Effects of four novel root-end filling materials on the viability of periodontal ligament fibroblasts. Restor Dent Endod. 43:e242018. View Article : Google Scholar : PubMed/NCBI

264 

Camilleri J, Sorrentino F and Damidot D: Investigation of the hydration and bioactivity of radiopacified tricalcium silicate cement, Biodentine and MTA Angelus. Dent Mater. 29:580–593. 2013. View Article : Google Scholar : PubMed/NCBI

265 

Kim JR, Nosrat A and Fouad AF: Interfacial characteristics of Biodentine and MTA with dentine in simulated body fluid. J Dent. 43:241–247. 2015. View Article : Google Scholar

266 

Gomes Cornélio AL, Salles LP, Campos da Paz M, Cirelli JA, Guerreiro-Tanomaru JM and Tanomaru Filho M: Cytotoxicity of Portland cement with different radiopacifying agents: A cell death study. J Endod. 37:203–210. 2011. View Article : Google Scholar : PubMed/NCBI

267 

Akbulut MB, Uyar Arpaci P and Unverdi Eldeniz A: Effects of novel root repair materials on attachment and morphological behaviour of periodontal ligament fibroblasts: Scanning electron microscopy observation. Microsc Res Tech. 79:1214–1221. 2016. View Article : Google Scholar : PubMed/NCBI

268 

Escobar-Garcia DM, Aguirre-Lopez E, Mendez-Gonzalez V and Pozos-Guillen A: Cytotoxicity and initial biocompatibility of endodontic biomaterials (MTA and Biodentine™) used as root-end filling materials. Biomed Res Int. 2016:79269612016. View Article : Google Scholar

269 

Futami T, Fujii N, Ohnishi H, Taguchi N, Kusakari H, Ohshima H and Maeda T: Tissue response to titanium implants in the rat maxilla: Ultrastructural and histochemical observations of the bone-titanium interface. J Periodontol. 71:287–298. 2000. View Article : Google Scholar : PubMed/NCBI

270 

Kou PM and Babensee JE: Macrophage and dendritic cell phenotypic diversity in the context of biomaterials. J Biomed Mater Res A. 96:239–260. 2011. View Article : Google Scholar

271 

Gratchev A, Guillot P, Hakiy N, Politz O, Orfanos CE, Schledzewski K and Goerdt S: Alternatively activated macrophages differentially express fibronectin and its splice variants and the extracellular matrix protein betaIG-H3. Scand J Immunol. 53:386–392. 2001. View Article : Google Scholar : PubMed/NCBI

272 

Brackett MG, Lewis JB, Messer RL, Lei L, Lockwood PE and Wataha JC: Dysregulation of monocytic cytokine secretion by endodontic sealers. J Biomed Mater Res B Appl Biomater. 97:49–57. 2011. View Article : Google Scholar : PubMed/NCBI

273 

Kabashima H, Nagata K, Maeda K and Iijima T: Involvement of substance P, mast cells, TNF-alpha and ICAM-1 in the infiltration of inflammatory cells in human periapical granulomas. J Oral Pathol Med. 31:175–180. 2002. View Article : Google Scholar : PubMed/NCBI

274 

Ribeiro RA, Souza-Filho MV, Souza MH, Oliveira SH, Costa CH, Cunha FQ and Ferreira HS: Role of resident mast cells and macrophages in the neutrophil migration induced by LTB4, fMLP and C5a des arg. Int Arch Allergy Immunol. 112:27–35. 1997. View Article : Google Scholar : PubMed/NCBI

275 

Gomes AC, Gomes-Filho JE and Oliveira SH: Mineral trioxide aggregate stimulates macrophages and mast cells to release neutrophil chemotactic factors: Role of IL-1beta, MIP-2 and LTB(4). Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 109:e135–e142. 2010. View Article : Google Scholar : PubMed/NCBI

276 

Baggiolini M: Chemokines and leukocyte traffic. Nature. 392:565–568. 1998. View Article : Google Scholar : PubMed/NCBI

277 

Gomes AC, Filho JE and de Oliveira SH: MTA-induced neutrophil recruitment: A mechanism dependent on IL-1beta, MIP-2, and LTB4. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 106:450–456. 2008. View Article : Google Scholar : PubMed/NCBI

278 

Cavalcanti BN, Rode Sde M, Franca CM and Marques MM: Pulp capping materials exert an effect on the secretion of IL-1β and IL-8 by migrating human neutrophils. Braz Oral Res. 25:13–18. 2011. View Article : Google Scholar : PubMed/NCBI

279 

Chang F, Kim JM, Choi Y and Park K: MTA promotes chemotaxis and chemokinesis of immune cells through distinct calcium-sensing receptor signaling pathways. Biomaterials. 150:14–24. 2018. View Article : Google Scholar

280 

Martinez FO and Gordon S: The M1 and M2 paradigm of macrophage activation: Time for reassessment. F000Prime Rep. 6:132014.

281 

Murray PJ, Allen JE, Biswas SK, Fisher EA, Gilroy DW, Goerdt S, Gordon S, Hamilton JA, Ivashkiv LB, Lawrence T, et al: Macrophage activation and polarization: Nomenclature and experimental guidelines. Immunity. 41:14–20. 2014. View Article : Google Scholar : PubMed/NCBI

282 

Zhu X, Yuan Z, Yan P, Li Y, Jiang H and Huang S: Effect of iRoot SP and mineral trioxide aggregate (MTA) on the viability and polarization of macrophages. Arch Oral Biol. 80:27–33. 2017. View Article : Google Scholar : PubMed/NCBI

283 

Braga JM, Oliveira RR, Martins RC and Ribeiro Sobrinho AP: The effects of a mineral trioxide aggregate-based sealer on the production of reactive oxygen species, nitrogen species and cytokines by two macrophage subtypes. Int Endod J. 47:909–919. 2014. View Article : Google Scholar

284 

Rezende TM, Vieira LQ, Cardoso FP, Oliveira RR, de Oliveira Mendes ST, Jorge ML and Ribeiro Sobrinho AP: The effect of mineral trioxide aggregate on phagocytic activity and production of reactive oxygen, nitrogen species and arginase activity by M1 and M2 macrophages. Int Endod J. 40:603–611. 2007. View Article : Google Scholar : PubMed/NCBI

285 

Yuan Z, Zhu X, Li Y, Yan P and Jiang H: Influence of iRoot SP and mineral trioxide aggregate on the activation and polarization of macrophages induced by lipopolysaccharide. BMC Oral Health. 18:562018. View Article : Google Scholar : PubMed/NCBI

286 

Yeh HW, Chiang CF, Chen PH, Su CC, Wu YC, Chou L, Huang RY, Liu SY and Shieh YS: Axl involved in mineral trioxide aggregate induces macrophage polarization. J Endod. 44:1542–1548. 2018. View Article : Google Scholar : PubMed/NCBI

287 

da Silva GN, Braz MG, de Camargo EA, Salvadori DM and Ribeiro DA: Genotoxicity in primary human peripheral lymphocytes after exposure to regular and white mineral trioxide aggregate. Oral Surg Oral Med Oral Pathol Oral Radiol Endod. 102:e50–e54. 2006. View Article : Google Scholar : PubMed/NCBI

288 

Barczak K, Palczewska-Komsa M, Nowicka A, Chlubek D and Buczkowska-Radlinska J: Analysis of the activity and expression of cyclooxygenases COX1 and COX2 in THP-1 monocytes and macrophages cultured with Biodentine™ Silicate cement. Int J Mol Sci. 21:22372020. View Article : Google Scholar

289 

Khedmat S, Dehghan S, Hadjati J, Masoumi F, Nekoofar MH and Dummer PM: In vitro cytotoxicity of four calcium silicate-based endodontic cements on human monocytes, a colorimetric MTT assay. Restor Dent Endod. 39:149–154. 2014. View Article : Google Scholar : PubMed/NCBI

290 

Chiang YC, Chang HH, Wong CC, Wang YP, Wang YL, Huang WH and Lin CP: Nanocrystalline calcium sulfate/hydroxyapatite biphasic compound as a TGF-β1/VEGF reservoir for vital pulp therapy. Dent Mater. 32:1197–1208. 2016. View Article : Google Scholar : PubMed/NCBI

Related Articles

Journal Cover

July-2021
Volume 48 Issue 1

Print ISSN: 1107-3756
Online ISSN:1791-244X

Sign up for eToc alerts

Recommend to Library

Copy and paste a formatted citation
x
Spandidos Publications style
Song W, Li S, Tang Q, Chen L and Yuan Z: <em>In vitro</em> biocompatibility and bioactivity of calcium silicate‑based bioceramics in endodontics (Review). Int J Mol Med 48: 128, 2021.
APA
Song, W., Li, S., Tang, Q., Chen, L., & Yuan, Z. (2021). <em>In vitro</em> biocompatibility and bioactivity of calcium silicate‑based bioceramics in endodontics (Review). International Journal of Molecular Medicine, 48, 128. https://doi.org/10.3892/ijmm.2021.4961
MLA
Song, W., Li, S., Tang, Q., Chen, L., Yuan, Z."<em>In vitro</em> biocompatibility and bioactivity of calcium silicate‑based bioceramics in endodontics (Review)". International Journal of Molecular Medicine 48.1 (2021): 128.
Chicago
Song, W., Li, S., Tang, Q., Chen, L., Yuan, Z."<em>In vitro</em> biocompatibility and bioactivity of calcium silicate‑based bioceramics in endodontics (Review)". International Journal of Molecular Medicine 48, no. 1 (2021): 128. https://doi.org/10.3892/ijmm.2021.4961